# US 5,350,157 A · Method for lining a continuous casting distributor with a refractory material, distributor and refractory material resulting from said method > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,350,157 A - Document ID: US5350157A - Status: Granted - Kind: A - Application number: 07/966,464 - Filed: 1992-10-26 - Granted: 1994-09-27 - Earliest claimed: 1991-11-04 - Assignees: Sollac; Le Laboratoire Metallurgique - Inventors: Jacques Poirier; Gilbert Provost; Jean Martin; Jean Rozieres - Web page: https://patentgrep.com/patent/US5350157A ## CPC - C04B 35/03: based on magnesium oxide, calcium oxide or oxide mixtures derived from dolomite - C04B 35/66: Monolithic refractories or refractory mortars, including those whether or not containing clay {(making or repairing of linings F27D1/16)} - C04B: LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE {(roofing granules E04D7/005)}; CERAMICS (devitrified glass-ceramics C03C10/00); REFRACTORIES; TREATMENT OF NATURAL STONE ## Abstract Method for lining a distributor for the continuous casting of metals, in particular steel, comprising preparing material for constituting a wear-resistant refractory lining of the distributor with raw natural dolomite, or raw natural calcite, or a mixture of these two materials, which are chosen with a particle size of between 0 and 5 mm, incorporating in this raw material a binder in proportions of 0.4 to 5% by weight and a mineral or organic plasticizer in proportions of 0.2 to 3% by weight and, after the lining has been placed in position on the distributor in the aqueous form, proceeding to the decarbonation of this lining in the course of its drying and baking, characterized in that the method further comprises incorporating in the material of the lining at least one compound having the property of shrinking at temperatures lower than about 700.degree. C. This compound is preferably a hydroxide of an alcaline earth metal or a mixture of such hydroxides incorporated in the lining material in the proportion of 5 to 20%. The invention also provides a lining for a distributor and a distributor provided with this lining. ## Claims ### Claim 1 A method for lining a distributor for the continuous casting of metals comprising the steps of: preparing a wear-resistant refractory lining material for said distributor comprising a material selected from the group consisting of raw natural dolomite, raw natural calcite, and a mixture thereof, choosing for said selected raw material a particle size of between 0 and 5 mm, adding to said selected raw material a binder in a proportion of 0.4 to 5% by weight and a plasticizer in a proportion of 0.2 to 3% by weight, putting said lining material in an aqueous form and putting it in position in said distributor, thereafter drying and baking said lining material, decarbonating said lining material in the course of said drying and baking, said method further comprising adding to said lining material at least a compound different from said binder and plasticizer and having a property of shrinking at temperatures below about 700.degree. C. ### Claim 2 (depends on 1) The method according to claim 1, wherein said plasticizer is a mineral plasticizer. ### Claim 3 (depends on 1) The method according to claim 1, wherein said plasticizer is an organic plasticizer. ### Claim 4 A method for lining a distributor for the continuous casting of metals comprising the steps of: preparing a wear-resistant refractory lining material for said distributor comprising a material selected from the group consisting of raw natural dolomite, raw natural calcite, and a mixture thereof, choosing for said selected raw material a particle size of between 0 and 5 mm, adding to said selected raw material a binder in a proportion of 0.4 to 5% by weight and a plasticizer in a proportion of 0.2 to 3% by weight, putting said lining material in an aqueous form and putting it in position in said distributor, thereafter drying and baking said lining material, decarbonating said lining material in the course of said drying and baking, said method further comprising adding to said lining material at least a compound having a property of shrinking at temperatures below about 700.degree. selected from the group consisting of a hydroxide of an alkaline earth metal and a mixture of said hydroxides in a proportion of 5 to 20% by weight. ### Claim 5 (depends on 1) The method according to claim 1, wherein said particle size is between 0 and 1 mm. ### Claim 6 (depends on 1) The method according to claim 1, comprising choosing sodium silicate as said binder. ### Claim 7 (depends on 1) The method according to claim 1, comprising choosing clay as said plasticizer. ### Claim 8 (depends on 1) The method according to claim 1, wherein said distributor is a distributor for the continuous casting of steel.