# US 5,349,000 A · Extrudable polyvinyl alcohol compositions containing polyester-polyether block copolymers > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,349,000 A - Document ID: US5349000A - Status: Granted - Kind: A - Application number: 08/023,031 - Filed: 1993-02-25 - Granted: 1994-09-20 - Earliest claimed: 1993-02-25 - Assignees: Air Products and Chemicals, Inc. - Inventors: Lloyd M. Robeson; Jeffrey A. Kuphal; Amir Famili - Web page: https://patentgrep.com/patent/US5349000A ## CPC - C08L 29/04: Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids - C08L 67/025: {containing polyether sequences} - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) ## Abstract In a melt extrudable polyvinyl alcohol composition consisting essentially of polyvinyl alcohol and plasticizer, which has been made melt extrudable by adding sufficient energy to the polyvinyl alcohol to both melt and substantially eliminate the crystallinity in the melt while simultaneously removing energy from the melt at a rate sufficient to avoid decomposition of the polyvinyl alcohol, the improvement which comprises 5 to 25 wt % poly(butylene terephthalate)-polytetrahydrofuran block copolymer for improved impact resistance. ## Claims ### Claim 1 In a melt extrudable polyvinyl alcohol composition comprising polyvinyl alcohol and plasticizer, the improvement for providing good impact efficiency which comprises 8 to 25 wt % thermoplastic polyester-polyether block copolymer, based on total composition. ### Claim 2 (depends on 1) The melt extrudable polyvinyl alcohol composition of claim 1 in which the polyvinyl alcohol is 75-99 mole % hydrolyzed and has a degree of polymerization of 200-2500. ### Claim 3 (depends on 1) The melt extrudable composition of claim 1 which comprises 8-20 wt % block copolymer. ### Claim 4 (depends on 1) The melt extrudable composition of claim 1 in which the block copolymer is 15-65 wt % polyester and 35-85 wt % polyether. ### Claim 5 (depends on 1) The melt extrudable composition of claim 1 in which the block copolymer is comprised of a multiplicity of recurring intralinear, long-chain and short-chain ester units connected head to tail through ester linkages with the long-chain ester units being represented by the structure: ##STR4## and the short-chain ester units being represented by the structure: ##STR5## where A is a divalent radical remaining after removal of the terminal hydroxy groups of a poly(tetrahydrofuran) glycol having a molecular weight (Mn) of from about 400 to about 4,000; B is a divalent radical remaining after removal of hydroxyl groups from ethylene glycol, butanediol or cyclohexane dimethanol; and R.sub.1 and R.sub.2 are independently 1,4-phenylene, 1,3-phenylene, naphthalene or cyclohexylene radicals. ### Claim 6 (depends on 5) The melt extrudable composition of claim 5 in which the block copolymer is poly(butylene terephthalate)-polytetrahydrofuran, poly(ethylene terephthalate)-polytetrahydrofuran, poly(ethylene isophthalate)-polytetrahydrofuran, poly(1,4-cyclohexylene terephthalate)-polytetrahydrofuran, or poly(1,4-cyclohexylene isophthalate)-polytetrahydrofuran. ### Claim 7 In a melt extrudable polyvinyl alcohol composition comprising polyvinyl alcohol which is 75-99 mole % hydrolyzed and has a degree of polymerization from 200-2500 and plasticizer, the improvement for providing good impact efficiency which comprises 8to 25 to wt % thermoplastic polyester-polyether block copolymer, based on total composition, which is comprised of a multiplicity of recurring intralinear, long-chain and short-chain ester units connected head to tail through ester linkages with the long-chain ester units being represented by the structure: ##STR6## and the short-chain ester units being represented by the structure: ##STR7## where A is a divalent radical remaining after removal of the terminal hydroxy groups of a poly(tetrahydrofuran) glycol having a molecular weight (Mn) of from about 400 to about 4,000; B is a divalent radical remaining after removal of hydroxyl groups from ethylene glycol, butanediol or cyclohexane dimethanol; and R.sub.1 and R.sub.2 are independently 1,4-phenylene, 1,3-phenylene, naphthalene or cyclohexylene radicals. ### Claim 8 (depends on 7) The melt extrudable composition of claim 7 in which B is a divalent radical remaining after removal of hydroxyl groups from butanediol. ### Claim 9 (depends on 7) The melt extrudable composition of claim 7 in which R.sub.1 and R.sub.2 are 1,4-phenylene radicals. ### Claim 10 (depends on 7) The melt extrudable composition of claim 7 in which the block copolymer is poly(butylene terephthalate)-polytetrahydrofuran block copolymer. ### Claim 11 (depends on 7) The melt extrudable composition of claim 7 in which the polyvinyl alcohol is 85-98 mole % hydrolyzed. ### Claim 12 (depends on 7) The melt extrudable composition of claim 7 which comprises 8-20 wt % block copolymer. ### Claim 13 In a melt extrudable polyvinyl alcohol composition comprising polyvinyl alcohol which is 85-98 mole % hydrolyzed and has a degree of polymerization from 200-2500 and plasticizer, the improvement for providing good impact efficiency which comprises 8 to 25 wt % thermoplastic poly(butylene terephthalate)-polytetrahydrofuran block copolymer, based on total composition. ### Claim 14 (depends on 13) The melt extrudable composition of claim 13 in which the block copolymer is 15-65 wt % polyester and 35-85 wt % polyether. ### Claim 15 (depends on 14) The melt extrudable composition of claim 14 which comprises 8-20 wt % block copolymer. ### Claim 16 (depends on 15) The melt extrudable composition of claim 15 in which the plasticizer is glycerine. ### Claim 17 (depends on 1) An article made by melt extruding the composition of claim 1. ### Claim 18 (depends on 7) An article made by melt extruding the composition of claim 7. ### Claim 19 (depends on 13) An article made by melt extruding the composition of claim 13.