# US 5,348,994 A · Polymer-modified functionalized asphalt compositions and methods of preparation (C-2747) > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,348,994 A - Document ID: US5348994A - Status: Granted - Kind: A - Application number: 08/041,079 - Filed: 1993-04-01 - Granted: 1994-09-20 - Earliest claimed: 1992-03-05 - Assignees: Exxon Research & Engineering Co. - Inventors: Martin L. Gorbaty; Dennis G. Peiffer; Daniel J. McHugh - Web page: https://patentgrep.com/patent/US5348994A ## CPC - C08L 95/00: Compositions of bituminous materials, e.g. asphalt, tar, pitch - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) ## Abstract Disclosed in this invention are novel road paving binder compositions and the method of making same. The compositions are made by combining an asphalt that contains sulfonate or sulfonic acid groups, a polymer preferably of butyl rubbers, styrene-butadiene linear diblock polymer, styrene-butadiene-styrene linear or radial triblock polymer and EPDM that has been sulfonated, and mixtures thereof, and a basic neutralizing agent that contains cations having a valence from +1 to +3. The amounts of each are effective to allow formation of one continuous phase or two interdispersed phases that do not segregate on standing at elevated temperatures associated with road paving. The amount of polymer is an amount less than 7 wt. % of total polymer-asphalt composition that is sufficient to produce an asphaltic composition having a viscosity at 135.degree. C. in the range of from about 150 cPs to about 2000 cPs or from about 3000 cPs to about 8000 cPs. The novel road paving asphaltic compositions have improved viscoelasticity, softening point, and storage stability. The compositions can be used as binders in road paving applications. ## Claims ### Claim 1 A method of making a road paving binder composition, which comprises combining a basic neutralizing agent, a sulfonated asphalt, and a sulfonated polymer selected from the group consisting of styrene-butadiene styrene linear and radial triblock polymers, styrene-butadiene linear diblock polymers sulfonated at the sites of olefinic unsaturation, sulfonated butyl rubbers and sulfonated EPDM and mixtures thereof, wherein the sulfonation is from.1 to 100 meq SO.sub.3 H per 100g of polymer, wherein the polymer is present in an amount by weight percent of total composition that is sufficient to maintain the viscosity of the composition in the range from about 150 to about 2000 cPs or from about 3000 to about 8000 cPs measured at 135.degree. C., wherein said amount is equal to or less than about 7 wt % when the polymer is sulfonated styrene-butadiene or sulfonated styrene-butadiene-styrene, and from greater than zero to 4 wt % when the polymer is sulfonated EPDM or sulfonated butyl rubber, to form a blend of asphalt and polymer having the asphalt and polymer interdispersed in at least one continuous phase such that the blend is storage stable and substantially phase compatible having a softening point variation between a sample of the top third and bottom third of the blend stored at elevated temperature equal to or less than about 4.degree. C. ### Claim 2 (depends on 1) The method of claim 1 wherein the asphalt and polymer are each sulfonated and neutralized separately, then combined. ### Claim 3 (depends on 1) The method of claim 1 wherein the polymer is sulfonated and neutralized, the asphalt is sulfonated, the polymer and asphalt are combined, then the mixture is neutralized. ### Claim 4 (depends on 1) The method of claim 1 wherein the polymer is blended with the asphalt, and the blend is sulfonated then neutralized. ### Claim 5 (depends on 4) The method of claim 4 wherein the polymer is selected from the group consisting of styrene butadiene diblock and styrene butadiene-styrene linear and radial triblock copolymers. ### Claim 6 (depends on 1) The method of claim 1 wherein the basic neutralizing agent is selected from the group consisting of ammonia, amines and bases that contain cations selected from the group consisting of Group IA, IIA, IIIA, and Group IB and VIIB of the periodic table and mixtures thereof. ### Claim 7 (depends on 1) The method of claim 1 wherein the basic neutralizing agent is selected from the group consisting of zinc oxide and calcium oxide. ### Claim 8 (depends on 1) The method of claim 1 wherein the sulfonated asphalt, sulfonated neutralized polymer and basic neutralizing agent are combined in situ at a temperature above about 140.degree. C. ### Claim 9 (depends on 11) The method of claim 11 wherein the basic neutralizing agent is present in excess of that required to neutralize the sulfonated polymer sulfonated asphalt blend. ### Claim 10 A road paving binder composition, comprising a base-neutralized blend of a sulfonated asphalt and a sulfonated polymer selected from the group consisting of styrene-butadiene styrene linear and radial triblock polymers, styrene-butadiene linear diblock polymers sulfonated at the sites of olefinic unsaturation, sulfonated butyl rubber and sulfonated EPDM, wherein the sulfonation is from 1 to 100 meq SO.sub.3 H per 100 g of polymer, wherein the polymer is present in an amount by weight percent of total composition that is sufficient for the blend to have a viscosity in a range of from about 150 to about 2000 cPs or from about 3000 to about 8000 cPs measured at 135.degree. C., wherein said amount is equal to or less than about 7 wt % when the polymer is sulfonated styrene-butadiene or sulfonated styrene-butadiene-styrene, wherein said amount is from greater than zero to 4 wt % when the polymer is sulfonated EPDM, or sulfonated butyl rubber wherein the blend has the asphalt and polymer interdispersed in at least one continuous phase such that the blend is storage stable and substantially phase compatible having a softening point variation between a sample of the top third and bottom third of a sample of the blend stored at elevated temperatures equal to or less than about 4.degree. C. ### Claim 11 (depends on 10) The composition of claim 10 wherein the continuous phase at any point of the blend is the same. ### Claim 12 (depends on 10) The composition of claim 10 wherein the continuous phase i s polymer. ### Claim 13 (depends on 10) The composition of claim 10 wherein the continuous phase is asphalt. ### Claim 14 (depends on 10) The composition of claim 10 wherein the continuous phase is polymer and asphalt. ### Claim 15 (depends on 10) The composition of claim 10 wherein the neutralized mixture of asphalt and polymer mixture contains cations of a basic neutralizing agent having a valence of from +1 to +3. ### Claim 16 (depends on 10) The composition of claim 10 wherein the sulfonation is from 3 to 60 meq SO.sub.3 H per 100 g of polymer.