# US 5,348,762 A · Process for the production of conductive layers > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,348,762 A - Document ID: US5348762A - Status: Granted - Kind: A - Application number: 08/062,038 - Filed: 1993-05-14 - Granted: 1994-09-20 - Earliest claimed: 1991-07-02 - Assignees: Ciba-Geigy Corporation - Inventors: Walther Hofherr; Ernst Minder; Bruno Hilti; Jean-Philippe Ansermet - Web page: https://patentgrep.com/patent/US5348762A ## CPC - C09D 5/24: Electrically-conducting paints {(conductive materials H01B1/00)} - H01B 1/121: {Charge-transfer complexes} - C09D: COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR (cosmetics A61K; processes for applying liquids or other fluent materials to surfaces, in general, B05D; staining wood B27K5/02; glazes or vitreous enamels C03C; natural resins, French polish, drying-oils, driers, turpentine, per se, C09F; polishing compositions other than French polish, ski waxes C09G; adhesives or use of materials as adhesives C09J; materials for sealing or packing joints or covers C09K3/10; materials for stopping leaks C09K3/12; processes for the electrolytic or electrophoretic production of coatings C25D) - H01B: CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES (selection for magnetic properties H01F1/00; waveguides H01P {; printed circuits H05K}) ## Abstract A process for the production of a conductive layer on a substrate, said conductive layer comprising a network of crystal needles of conductive radical cation salts based on tetrathiotetracenes, tetraselenotetracenes or tetratellurotetracenes and chlorine, bromine, iodine or copper dichloride, and said network is embedded in a polymer matrix, by coating at least one side of said substrate with a) a suspension of crystal needles of the radical cation salts of formula I in an inch solvent which may additionally contain a thermoplastic polymer or at least one starting compound for a thermosetting polymer, or b) a solution (b1) of a tetrathiotetracene, tetraselenotetracene or tetratellurotetracene, (b2) of a monomeric, oligomeric or polymeric organic compound which contains chlorine, bromine or iodone and, when heated with these tetracenes, forms a radical cation salt, or of anhydrous CuCl.sub.2, a CuCl.sub.2 aquo complex or a CuCl.sub.2 solvent complex, and (C3) of a thermoplastic polymer or at least one starting compound for a thermosetting polymer, in an inert solvent, and subsequently evaporating the solvent, which process comprises applying said layer by spraying the suspension a) or solution b) from nozzles on to the substrate. Very fine meshed, dense and isotropic crystal needle networks are obtained. The coatings exhibit rapid surface discharges and are suitable for use as electostatic coatings or, on account of their good electrical conductivities, as electrode material for display elements. ## Claims ### Claim 1 A process for preparing a conductive layer on a substrate wherein said conductive layer is a network of crystal needles embedded in a polymer matrix and said crystal needles consist essentially of a conductive radial cation salt of formula (I) ##STR3## wherein X is S, Se or Te, n is a value from 0.3 to 0.9, R.sub.1 is H, F, Cl or CH.sub.3, and R.sub.2, R.sub.3 and R.sub.4 are H, or R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each F or CH.sub.3, or R.sub.1 and R.sub.2 are each F, Cl or CH.sub.3 and R.sub.3 and R.sub.4 are each H, or R.sub.1 and R.sub.3 or R.sub.1 and R.sub.4 are each H, or R.sub.1 and R.sub.3 or R.sub.1 and R.sub.4 are each F and R.sub.2 and R.sub.4 or R.sub.2 and R.sub.3 are each H, and Y is Cl, Br, I or CuCl.sub.2, which process comprises (1) spraying a solution onto said substrate, wherein the solution comprises an inert solvent and (b1) a compound of formula II ##STR4## (b2) anhydrous CuCl.sub.2, a CuCl.sub.2 aquo complex, a CuCl.sub.2 solvent complex or a monomeric, oligomeric or polymeric halogenated aromatic compound containing chlorine, bromine or iodine, which forms the radical cation salt of formula I when heated with a compound of formula II, and (b3) a thermoplastic polymer or at least one starting compound for a thermosetting polymer, wherein the solution is heated to a temperature of from 50.degree. to 350.degree. C. before, during or after the spraying step, and (2) subsequently evaporating the solvent. ### Claim 2 (depends on 1) A process of claim 1 wherein the solution is sprayed through a nozzle having an orifice with a diameter of from 0.1 to 10 mm. ### Claim 3 (depends on 2) A process of claim 2 wherein a pressure is required for spraying and the pressure is produced by a propellant gas. ### Claim 4 (depends on 3) A process according to claim 3, wherein the propellent gas is argon or nitrogen. ### Claim 5 (depends on 3) A process according to claim 3, wherein the pressure of the propellant gas is from 10.sup.4 to 10.sup.6 Pa. ### Claim 6 (depends on 3) A process according to claim 3, wherein the temperature of the nozzle heads is in the range from room temperature to 250.degree. C. ### Claim 7 (depends on 3) A process according to claim 3, wherein the distance of the nozzle heads from the substrate is from 1 to 100 cm. ### Claim 8 (depends on 3) A process according to claim 3, wherein one or more than one nozzle head is used simultaneously. ### Claim 9 (depends on 3) A process according to claim 3, wherein the concentration of the compounds of formula II is 0.1% by weight to 20% by weight, based on the solution. ### Claim 10 (depends on 3) A process according to claim 3, wherein the concentration of the thermoplastic polymers or starting compounds for thermosetting polymers in the solution is up to 60% by weight. ### Claim 11 (depends on 3) A process according to claim 3, wherein the substrate is preheated. ### Claim 12 (depends on 3) A process according to claim 3, wherein the compound of formula I is selected from the group consisting of (tetrrathiotetracene)Cl.sub.0.5, (tetrathiotetracene)Br.sub.0.5, (tetrathiotetracene)I.sub.0.75,(tetraselenotetracene)Cl.sub.0.5, (tetraselenotetracene)Br.sub.0.5, (2-fluoro- or 2,3-difluorotetrathio- or-tetrraselenotetracene)Cl.sub.0.5, (2-fluoro- or 2,3-difluorotetrathio- or -tetraselenotetracene)Br.sub.0.5 and (tetrathiotetracene)(CuCl.sub.2).sub.0.4 to 0.6. ### Claim 13 (depends on 1) A process according to claim 1, wherein the thermoplastic polymer is selected from the group consisting of polyolefins, polystyrene, polyvinyl chloride, polyvinylidene chloride, polyvinylidene fluoride, polyacrylates, polymethacrylates, polyamides, polyesters, polycarbonates, aromatic polysulfones, aromatic polyethers, aromatic polyether sulfones, polyimides and polyvinyl carbazole. ### Claim 14 (depends on 1) A process according to claim 1, wherein the solvent is evaporated in the temperature range from 50.degree. to 250.degree. C. ### Claim 15 (depends on 1) A process according to claim 1, wherein the ratio of the organic compound which contains chlorine, bromine or iodine to the compounds of formula II is from 10:1 to 1:5. ### Claim 16 (depends on 1) A process according to claim 1, wherein the halogenated organic compound is selected from the group consisting of tetrabromomethane, bromoform, trichlorobromomethane, hexachloropropene, hexachlorocyclopropane, hexachlorocyclopentadiene, hexachloroethane, N-chlorosuccinimide, octachloropropane, n-octachlorobutane, n-decachlorobutane, tetrabromoethane, hexabromoethane, tetrabromo-o-benzoquinone, 2,4,4,6-tetrabromo-2,5-cyclohexadienone, hexabromobenzene, chloranil, hexachloroacetone, 1,4,5,6,7,7-hexachloro-5-norbornene-2,3-dicarboxylic acid, 1,2,5,6,9, 10-hexabromocyclododecane, tetrachloroethylene, perchlorocyclopentadiene, perchlorobutadiene, dichloroacetaldehyde diethyl acetal, 1,4-dichlorobut-2-ene, 1,3-dichlorobut-2-ene, 3,4-dichlorobut-1-ene, tetrachlorocyclopropene, 1,3-dichloroacetone, 2,3,5,6-hexachloro-p-xylene, 1,4-bis(trichloromethyl)benzene, 1,3-dibromopropane, 1,6-dibromohexane, ethyl 3-chloropropionate, 3-chlorotoluene, methyl 2-chloropropionate, 2-chloroacrylonitrile, ethyl trichloroacetate, 1,2,3-trichloropropane, 1,1,2-trichloroethane, butyl chloroformate, trichloroethylene, 2,3-dichloromaleic anhydride, 1,12-dibromododecane, .alpha.,.alpha.'-dibromo-p-xylene, .alpha.,.alpha.'-dichloro-o-xylene, phenacyl chloride or bromide, 1,10-dibromodecane, .alpha.,.alpha.'-dichloro-p-xylene, .alpha.,.alpha.'-dibromo-m-xylene, iodoacetonitrile, 2,3-odichloro-5,6-dicyanobenzoquinone, methyl 2,3-dichloropropionate, 1-bromo-2-chloroethane, 1-bromo-2-chloropropane, 2-bromoethyl chloroformate, ethyl iodoacetate, N-chloro-, N-bromo- or N-iodosuccinimide or N-iodophthalimide, or mixtures thereof. ### Claim 17 (depends on 1) A process according to claim 1, wherein the halogenated organic compound is tri(C.sub.1 -C.sub.6 alkyl)ammonium hydrochloride and an aqueous solution of H.sub.2 O.sub.2 is additionally used concurrently. ### Claim 18 A process for preparing a conductive layer on a substrate wherein said conductive layer is a network of crystal needles embedded in a polymer matrix and said crystal needles consist essentially of a conductive radial cation salt of formula (I) ##STR5## wherein X is S, Se or Te, n is a value from 0.3 to 0.9, R.sub.1 is H, F, Cl or CH.sub.3, and R.sub.2, R.sub.3 and R.sub.4 are H, or R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each F or CH.sub.3, or R.sub.1 and R.sub.2 are each F, Cl or CH.sub.3 and R.sub.3 and R.sub.4 are each H, or R.sub.1 and R.sub.3 or R.sub.1 and R.sub.4 are each H, or R.sub.1 and R.sub.3 or R.sub.1 and R.sub.4 are each F and R.sub.2 and R.sub.4 or R.sub.2 and R.sub.3 are each H, and Y is Cl, Br, I or CuCl.sub.2, which process comprises (1) spraying a suspension of the crystal needles in an inert solution onto said substrate, wherein the suspension additionally contains a dissolved thermoplastic polymer or at least one starting compound for a thermoplastic polymer, and (2) subsequently evaporating the solvent. ### Claim 19 (depends on 18) A process of claim 18 wherein the suspension is heated to a temperature of from 20.degree. C. to 200.degree. C. before, during or after the spraying step. ### Claim 20 (depends on 18) A process of claim 18 wherein the concentration of the radical cation salt of formula I is from 0.1% by weight to 20% by weight, based on the weight of the suspension.