# US 5,348,108 A · Rolling cone bit with improved wear resistant inserts > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,348,108 A - Document ID: US5348108A - Status: Granted - Kind: A - Application number: 07/895,594 - Filed: 1992-06-08 - Granted: 1994-09-20 - Earliest claimed: 1991-03-01 - Assignees: Baker Hughes Incorporated - Inventors: Danny E. Scott; Redd H. Smith; Gordon A. Tibbitts - Web page: https://patentgrep.com/patent/US5348108A ## CPC - E21B 10/567: with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts - B22F 7/06: of composite workpieces or articles from parts, e.g. to form tipped tools {(B22F7/002 takes precedence)} - E21B 10/52: with chisel- or button-type inserts - E21B 10/56: Button-type inserts (E21B10/52 takes precedence) - E21B 10/5676: {having a cutting face with different segments, e.g. mosaic-type inserts} - E21B 10/62: characterised by parts, e.g. cutting elements, which are detachable or adjustable (E21B10/64 takes precedence; for roller bits E21B10/20; for augers E21B10/44) - E21B: EARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS - B22F: WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER (making alloys by powder metallurgy C22C); APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER ## Abstract An improved earth-boring bit the rolling cone variety and an insert for use therein is provided. A superabrasive element is coated with at least one layer of metallic material. The superabrasive element then is placed in a receptacle cavity in a pre-formed hard metal jacket. The superabrasive element then is brazed or infiltrated to the hard metal jacket. Metallurgical and mechanical bonds between the superabrasive element, the at least one layer of metallic material on superabrasive element, the braze or infiltrant binder material, and the fracture-tough material of the hard metal jacket retain the superabrasive element in the cavity of the hard metal jacket. Improved earth-boring bits according to this embodiment of the present invention provide abrasion-resistant earth-boring bits of the rolling cutter variety. Such improved bits, and the inserts therefore, are formed without resort to high-temperature, high-pressure processes. ## Claims ### Claim 1 An insert for use in an earth-boring bit having a body and at least one bearing shaft depending downwardly and inwardly therefrom, at least one cutter cone mounted for rotation on the bearing shaft, the cutter cone having a plurality of sockets formed therein to receive the insert by fit, the insert comprising: a hard metal jacket formed of fracture-tough material, the hard metal jacket having at least one opening formed in an upper end thereof to define a receptacle cavity; and at least one superabrasive element secured in the receptacle cavity to form at least a portion of an exposed, wear-resistant working surface on the upper end of the insert, the wear-resistant working surface being surrounded at a peripheral edge thereof by the fracture-tough material of the hard metal jacket, wherein a majority of the wear-resistant working surface is formed of superabrasive and the fracture-tough material insulates the superabrasive element from shock loads encountered in operation. ### Claim 2 (depends on 1) The insert according to claim 1 wherein the superabrasive element is a thermally stable polycrystalline diamond having at least one layer of metallic material formed thereon, the thermally stable polycrystalline diamond secured in the receptacle cavity by both mechanical and metallurgical bonds between the thermally stable polycrystalline diamond, the at least one layer of metallic material, a binder material, and the fracture-tough material of the hard metal jacket. ### Claim 3 (depends on 1) The insert according to claim 1 wherein the superabrasive element is polycrystalline diamond, the polycrystalline diamond formed integrally in the hard metal jacket by a high-pressure, high-temperature process. ### Claim 4 An earth-boring bit of the rolling cutter type, the earth-boring bit comprising: a bit body having at least one bearing shaft depending therefrom; at least one cutter cone rotatably mounted on the bearing shaft, the cutter cone having a plurality of sockets formed therein to receive mating cutting inserts; a plurality of cutting inserts secured by interference fit in the sockets in the cutter cone, the inserts including: a hard metal jacket formed of fracture-tough material, the hard metal jacket having at least one opening formed in an upper end thereof to define a receptacle cavity; and at least one superabrasive element secured in the receptacle cavity to form at least a portion of an exposed, wear-resistant working surface on the upper end of the insert, the wear-resistant working surface being surrounded at a peripheral edge thereof by the fracture-tough material of the hard metal jacket, wherein a majority of the wear-resistant working surface is formed of superabrasive and the fracture-tough material insulates the superabrasive element from shock loads encountered in operation. ### Claim 5 (depends on 4) The earth-boring bit according to claim 4 wherein the superabrasive element is a thermally stable polycrystalline diamond having at least one layer of metallic material formed thereon, the thermally stable polycrystalline diamond secured in the receptacle cavity by both mechanical and metallurgical bonds between the thermally stable polycrystalline diamond, the at least one layer of metallic material, a binder material, and the fracture-tough material of the hard metal jacket. ### Claim 6 (depends on 4) The earth-boring bit according to claim 4 wherein the superabrasive element is polycrystalline diamond, the polycrystalline diamond formed integrally in the hard metal jacket by a high-pressure, high-temperature process. ### Claim 7 A gage insert for use in a gage row of an earth-boring bit of the rolling cutter variety, the insert comprising: a hard metal jacket formed of a fracture-tough material and having at least one opening formed at a selected end thereof and defining an receptacle cavity therein; at least one superabrasive element having at least one layer of metallic material formed thereon; the superabrasive element secured in the receptacle cavity by both substantially mechanical bonds and substantially metallurgical bonds between the superabrasive element, the at least one layer of metallic material, the fracture-tough material, and a binder material; and wherein the superabrasive element forms an exposed working surface at the selected end of the insert and is surrounded at a peripheral edge thereof by the fracture-tough material of the hard metal jacket to prevent rapid degradation of the superabrasive in operation. ### Claim 8 (depends on 7) The gage insert according to claim 7 wherein the superabrasive element is a thermally stable polycrystalline diamond element. ### Claim 9 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material formed on the superabrasive element comprises a single layer formed of a metal selected from the group consisting of titanium, tantalum, tungsten, chromium, niobium, molybdenum, and manganese. ### Claim 10 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material formed on the superabrasive element is a single layer of tungsten. ### Claim 11 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer comprising a first layer of nickel, an intermediate layer of copper, and an outer layer of nickel, the compliant layer to redistribute stresses from the superabrasive element. ### Claim 12 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer formed of ductile metal, and an inner layer and an outer layer formed of a metal selected from the group consisting of titanium, tantalum, tungsten, chromium, niobium, molybdenum, and manganese. ### Claim 13 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer formed of ductile metal, and an inner layer and an outer layer formed of tungsten. ### Claim 14 (depends on 7) The gage insert according to claim 7 wherein the at least one layer of metallic material is substantially mechanically bonded to the superabrasive element and is substantially metallurgically bonded to the binder material and the fracture-tough material of hard metal jacket. ### Claim 15 (depends on 7) The insert according to claim 7 wherein an inner layer of the at least one layer of metallic material is substantially mechanically bonded to the superabrasive element and is substantially metallurgically bonded to a compliant layer, and an outer layer of the at least one layer of metallic material is substantially metallurgically bonded to the compliant layer, the binder material, and the fracture-tough material of the hard metal jacket. ### Claim 16 (depends on 7) The insert according to claim 7 wherein the fracture-tough material of the hard metal jacket is cemented tungsten carbide. ### Claim 17 (depends on 7) The insert according to claim 7 wherein the fracture-tough material of the hard metal jacket is selected from the group consisting of tungsten carbide, tungsten dicarbide, niobium carbide, tantalum carbide, chromium carbide, titanium carbide, molybdenum carbide, and mixtures thereof. ### Claim 18 (depends on 7) The insert according to claim 7 wherein the binder material is a low-temperature silver alloy braze. ### Claim 19 (depends on 7) The insert according to claim 7 wherein the binder material is an infiltrant material comprising substantially 5-65% by weight of manganese, up to substantially 35% by weight of zinc, and a balance of the infiltrant copper, the infiltrant material having a melting temperature less than substantially 1070 degrees Celsius. ### Claim 20 (depends on 7) The gage insert according to claim 7 wherein the at least one superabrasive element further comprises six triangular superabrasive elements, and the at least one receptacle cavity further comprises six triangular cavities substantially coextensive with each of the six triangular superabrasive elements. ### Claim 21 An improved earth-boring bit of the rolling cutter type, the earth-boring bit comprising: a bit body having at least one bearing shaft depending therefrom; at least one cutter rotatably mounted on the bearing shaft, the cutter cone having a plurality of sockets formed therein to receive mating cutting inserts; a plurality of cutting inserts in the sockets in the cutter cone, the inserts including: a hard metal jacket formed of a fracture-tough material and having at least one opening formed therein to define a receptacle cavity therein; at least one superabrasive element having a at least one layer of metallic material formed thereon; the superabrasive element secured in the receptacle cavity by a combination of substantially mechanically bonds and substantially metallurgical bonds between the superabrasive element, the at least one layer of metallic material, the fracture-tough material, and a binder material; wherein the superabrasive element forms an exposed working surface of the insert and is surrounded at a peripheral edge thereof by the fracture-tough material of the hard metal jacket to insulate the superabrasive element from shock loads encountered in operation. ### Claim 22 (depends on 21) The earth-boring bit according to claim 21 wherein the superabrasive element is a thermally stable polycrystalline diamond. ### Claim 23 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material formed on the superabrasive element comprises a single layer formed of a metal selected from the group consisting of titanium, tantalum, tungsten, chromium, niobium, molybdenum, and manganese. ### Claim 24 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material formed on the superabrasive element is a single layer of tungsten. ### Claim 25 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer comprising a first layer of nickel, an intermediate layer of copper, and an outer layer of nickel, the compliant layer to redistribute stresses from the superabrasive element. ### Claim 26 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer formed of ductile metal, and an inner layer and an outer layer formed of a metal selected from the group consisting of titanium, tantalum, tungsten, chromium, niobium, molybdenum, and manganese. ### Claim 27 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material formed on the superabrasive element includes a compliant layer formed of ductile metal, and an inner layer and an outer layer formed of tungsten. ### Claim 28 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one layer of metallic material is substantially mechanically bonded to the superabrasive element and is substantially metallurgically bonded to the binder material and the fracture-tough material of hard metal jacket. ### Claim 29 (depends on 21) The earth-boring bit according to claim 21 wherein an inner layer of the at least one layer of metallic material is substantially mechanically bonded to the superabrasive element and is substantially metallurgically bonded to a compliant layer, and an outer layer of the plurality of layers of metallic material is substantially metallurgically bonded to the compliant layer, the binder material, and the fracture-tough material of the hard metal jacket. ### Claim 30 (depends on 21) The earth-boring bit according to claim 21 wherein the fracture-tough material of the hard metal jacket is cemented tungsten carbide. ### Claim 31 (depends on 21) The earth-boring bit according to claim 21 wherein the fracture-tough material of the hard metal jacket is selected from the group consisting of tungsten carbide, tungsten dicarbide, niobium carbide, tantalum carbide, chromium carbide, titanium carbide, molybdenum carbide, and mixtures thereof. ### Claim 32 (depends on 21) The earth-boring bit according to claim 21 wherein the binder material is a low-temperature silver braze. ### Claim 33 (depends on 21) The earth-boring bit according to claim 21 wherein the binder material is an infiltrant material comprising substantially 5-65% by weight of manganese, up to substantially 35% by weight of zinc, and a balance of the infiltrant copper, the infiltrant material having a melting temperature less than substantially 1070 degrees Celsius. ### Claim 34 (depends on 21) The earth-boring bit according to claim 21 wherein the at least one superabrasive element further comprises six triangular superabrasive elements, and the at least one receptacle cavity further comprises six triangular cavities substantially coextensive with each of the six triangular superabrasive elements. ### Claim 35 An improved earth-boring bit of the rolling cutter type, the earth-boring bit comprising; a bit body having at least one bearing shaft depending therefrom; at least one cutter cone rotatably mounted on the bearing shaft, the cutter cone having a plurality of sockets formed therein to receive mating cutting inserts; a plurality of cutting inserts secured at one end thereof by interference fit in the sockets in the cutter cone, the inserts including; a hard metal jacket formed of a fracture-tough material and having an opening formed therein to define a generally cylindrical receptacle cavity therein; a generally cylindrical superabrasive element having a plurality of layers of metallic material formed thereon, the plurality of layers of metallic material including a layer of compliant material to absorb thermal stresses from the superabrasive element; the superabrasive element secured in the generally cylindrical receptacle cavity by both substantially mechanical bonds and substantially metallurgical bonds between the superabrasive element, the plurality of layers of metallic material, the material of the hard metal jacket, and a binder material; wherein the generally cylindrical superabrasive element forms a majority of an exposed working surface of the insert and is surrounded at a peripheral edge thereof by the fracture-tough material of the hard metal jacket to insulate the generally cylindrical superabrasive element from shock loads in operation. ### Claim 36 (depends on 35) The earth-boring bit according to claim 35 wherein the superabrasive element is a thermally stable polycrystalline diamond. ### Claim 37 (depends on 35) The earth-boring bit according to claim 35 wherein the layer of compliant material further comprises a first layer of nickel, an intermediate layer of copper, and an outer layer of nickel. ### Claim 38 (depends on 35) The earth-boring bit according to claim 35 wherein the plurality of layers of metallic material formed on the superabrasive element further includes an inner layer and an outer layer formed from metals selected from the group consisting of titanium, tantalum, tungsten, chromium, niobium, molybdenum, and manganese. ### Claim 39 (depends on 35) The earth-boring bit according to claim 35 wherein an inner layer of the plurality of layers of metallic material is mechanically bonded to the superabrasive element and is metallurgically bonded to the compliant layer, and an outer layer of the plurality of layers of metallic material is metallurgically bonded to the compliant layer and is metallurgically bonded to the binder material and the fracture-tough material of the hard metal jacket. ### Claim 40 (depends on 35) The earth-boring bit according to claim 35 wherein the fracture-tough material of the hard metal jacket is cemented tungsten carbide. ### Claim 41 (depends on 35) The earth-boring bit according to claim 35 wherein the fracture-tough material of the hard metal jacket is selected from the group consisting of tungsten carbide, tungsten dicarbide, niobium carbide, tantalum carbide, chromium carbide, titanium carbide, molybdenum carbide, and mixtures thereof. ### Claim 42 (depends on 35) The earth-boring bit according to claim 35 wherein the binder material is a low-temperature silver alloy braze. ### Claim 43 (depends on 35) The earth-boring bit according to claim 35 wherein the binder material is an infiltrant material comprising substantially 5-65% by weight of manganese, up to substantially 35% by weight of zinc, and a balance of the infiltrant copper, the infiltrant material having a melting temperature less than substantially 1070 degrees Celsius.