# US 5,347,098 A · Method of welding nickel or nickel alloy products > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,347,098 A - Document ID: US5347098A - Status: Granted - Kind: A - Application number: 07/913,186 - Filed: 1992-07-14 - Granted: 1994-09-13 - Earliest claimed: 1991-07-15 - Assignees: Nippon Steel Corporation; Aichi Sangyo Co., Ltd. - Inventors: Yasuo Murakami; Hideki Kashimura; Kiichi Katayama; Hiroshi Imaizumi; Toshio Katou; Hideaki Nakashima - Web page: https://patentgrep.com/patent/US5347098A ## CPC - B23K 35/383: {mainly containing noble gases or nitrogen} - B23K 9/173: and of a consumable electrode - B23K: SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM ## Abstract A method of welding metal products, at least one of which is made of nickel or a nickel alloy, comprises the steps of generating an arc between the products to be welded, serving as a positive pole, and a tungsten electrode held by a welding torch, serving as a negative pole. A shielding gas is emitted, consisting of an argon-based mixed gas containing one or both of hydrogen and helium, from a confining gas nozzle concentric with the tungsten electrode, thus confining the apparent flaring angle of the arc within 80 degrees. The welding torch is moved along the weld line while feeding the tip of a filler wire to a part of the molten pool directly below the arc. This method is applicable to the welding of metal products, at least one of which is made of nickel or a nickel alloy. ## Claims ### Claim 1 A pipe welding method that deposits a first weld bead in welding the circumference of butt-jointed pipes, at least one of the pipes comprising nickel or a nickel alloy, said pipe welding method comprising the steps of: generating an arc between the pipes to be welded together and a tungsten electrode held by a welding torch, the pipes serving as a positive pole and the tungsten electrode serving as a negative pole; emitting a shielding gas that comprises an argon-based mixed gas that contains at least one of hydrogen and helium from a confining gas nozzle concentric with the tungsten electrode and thereby confining the apparent flaring angle of the arc to a maximum of 80 degrees; and moving the welding torch along the weld line while feeding the tip of a filler wire to a part of the molten pool directly below the arc. ### Claim 2 (depends on 1) The pipe welding method of claim 1, wherein the pipes are double pipes, and wherein the pipes have an overlay comprising nickel or a nickel alloy. ### Claim 3 (depends on 1) The pipe welding method of claim 1, wherein at least one of the pipes is a double pipe having an inner pipe comprising nickel or a nickel alloy mechanically joined to an outer pipe, the double pipe having both ends thereof seal welded. ### Claim 4 (depends on 1) The pipe welding method of claim 1, wherein the argon-based mixed gas comprises 95-98% argon and 2-5% hydrogen. ### Claim 5 (depends on 1) The pipe welding method of claim 1, wherein the argon-based mixed gas comprises 40-50% argon and 50-60% helium. ### Claim 6 (depends on 1) The pipe welding method of claim 1, wherein the argon-based mixed gas comprises 45-55% argon, 40-50% helium and 2-5% hydrogen. ### Claim 7 (depends on 1) The pipe welding method of claim 1, wherein, in said step of emitting a shielding gas, the flow rate of the shielding gas emitted from the confining gas nozzle is maintained below a level above which a keyhole would be formed in the molten pool. ### Claim 8 (depends on 1) The pipe welding method of claim 1, wherein, in said step of emitting a shielding gas, the flow rate of the shielding gas emitted from the confining gas nozzle is 3-8 liters per minute. ### Claim 9 A pipe welding method that deposits second and subsequent weld beads in welding the circumference of butt-jointed pipes, at least one of the pipes comprising nickel or a nickel alloy, said pipe welding method comprising the steps of: generating an arc between the pipes to be welded together and a tungsten electrode held by a welding torch, the pipes serving as a positive pole and the tungsten electrode serving as a negative pole; emitting a shielding gas from a confining gas nozzle concentric with the tungsten electrode; and oscillating a first filler wire integrally with the welding torch in a direction perpendicular to the weld line with a predetermined amplitude and frequency and moving the first filler wire along the weld line while feeding the tip thereof to a part of the molten pool directly below the arc, and oscillating a second filler wire at the same frequency as the first filler wire but 180.degree. out of phase with the oscillation of the first filler wire, and moving the second filler wire along the weld line while feeding the tip thereof into the molten pool. ### Claim 10 (depends on 9) The pipe welding method of claim 9, wherein the pipes are double pipes, and wherein the pipes have an overlay comprising nickel or a nickel alloy. ### Claim 11 (depends on 9) The pipe welding method of claim 9, wherein at least one of the pipes is a double pipe having an inner pipe comprising nickel or a nickel alloy mechanically joined to an outer pipe, the double pipe having both ends thereof seal welded. ### Claim 12 (depends on 9) The pipe welding method of claim 9, wherein the shielding gas comprises an argon-based mixed gas that contains at least one of hydrogen and helium. ### Claim 13 (depends on 12) The pipe welding method of claim 12, wherein the argon-based mixed gas comprises 95-98% argon and 2-5% hydrogen. ### Claim 14 (depends on 12) The pipe welding method of claim 12, wherein the argon-based mixed gas comprises 40-50% argon and 50-60% helium. ### Claim 15 (depends on 12) The pipe welding method of claim 12, wherein the argon-based mixed gas comprises 45-55% argon, 40-50% helium and 2-5% hydrogen. ### Claim 16 (depends on 9) The pipe welding method of claim 9, wherein, in said step of emitting a shielding gas, the flow rate of the shielding gas emitted from the confining gas nozzle is maintained below a level above which a keyhole would be formed in the molten pool. ### Claim 17 (depends on 9) The pipe welding method of claim 9, wherein, in said step of emitting a shielding gas, the flow rate of the shielding gas emitted from the confining gas nozzle is 3-8 liters per minute. ### Claim 18 (depends on 9) The pipe welding method of claim 9, wherein, in said step of oscillating the first and second filler wires, the first and second filler wires are fed into the molten pool such that the first filler wire provides 80-90% of the deposited metal and the second filler wire provides 10-20% of the deposited metal. ### Claim 19 A pipe welding method that welds the circumference of butt-jointed pipes, at least one of the pipes comprising nickel or a nickel alloy, said pipe welding method comprising the steps of: generating an arc between the pipes to be welded together and a tungsten electrode held by a welding torch, the pipes serving as a positive pole and the tungsten electrode serving as a negative pole; emitting a shielding gas that comprises an argon-based mixed gas that contains at least one of hydrogen and helium from a confining gas nozzle concentric with the tungsten electrode and thereby confining the apparent flaring angle of the arc to a maximum of 80 degrees; and applying a first welding pass by moving the welding torch along the weld line while feeding the tip of a first filler wire into a part of the molten pool directly below the arc; and applying second and subsequent welding passes by confining the arc through said step of emitting the shielding gas, oscillating the first filler wire integrally with the welding torch in a direction perpendicular to the weld line with a predetermined amplitude and frequency and moving the first filler wire along the weld line while feeding the tip thereof to a part of the molten pool directly below the arc, and oscillating a second filler wire at the same frequency as the first filler wire but 180.degree. out of phase with the oscillation of the first filler wire, and moving the second filler wire along the weld line while feeding the tip thereof into the molten pool.