# US 5,346,940 A · Two-part fast curing RTV silicone for formed-on-part automotive gasket > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,346,940 A - Document ID: US5346940A - Status: Granted - Kind: A - Application number: 08/036,496 - Filed: 1993-03-24 - Granted: 1994-09-13 - Earliest claimed: 1993-03-24 - Assignees: Loctite Corporation - Inventors: David M. Brassard; Hans E. Haas; David W. Friedel - Web page: https://patentgrep.com/patent/US5346940A ## CPC - C08K 5/5415: containing at least one Si—O bond - C08L 83/04: Polysiloxanes - C08G 77/16: to hydroxy groups - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) - C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS ## Abstract A two-part RTV silicone preapplied compression gasket material for forming compression gaskets in place. The formulation includes a silanol terminated polyorganosiloxane, at least 5% by weight of the formulation of a tri- or tetra- methoxy or enoxy functional silane crosslinker, water, and, a condensation catalyst selected from the group consisting of stannous carboxylate compounds, dimethyl tin (IV) compounds and mixtures thereof. One of the two parts of the formulation includes the water component and the other of said two parts is a dry part and includes the crosslinker component. The formulation provides fast cure, fast development of compression set resistance and excellent ultimate compression set resistance. ## Claims ### Claim 1 A fast curing two-part RTV silicone formulation comprising: a silanol terminated polyorganosiloxane; at least 5% by weight of the formulation of a tri- or tetra- methoxy or enoxy functional silane crosslinker; water; and, a condensation catalyst selected from the group consisting of stannous carboxylate compounds, dimethyl tin (IV) compounds and mixtures thereof, the water being present in a first of said two parts and the second of said two parts being free of water and comprising said crosslinker component. ### Claim 2 (depends on 1) A formulation as in claim 1 wherein the said first part further comprises said silanol terminated polyorganosiloxane and said second part further comprises said condensation catalyst and a tri-methylsilyl terminated polyorganosiloxane. ### Claim 3 (depends on 2) A formulation as in claim 2 further comprising one or more fillers. ### Claim 4 (depends on 3) A formulation as in claim 3 wherein the stoichiometry thereof is adjusted to provide a mix ratio of the two parts of between 10:1 and 1:2, volume basis. ### Claim 5 A fast curing two-part RTV silicone formulation comprising: a silanol terminated polyorganosiloxane; at least 5% by weight of the formulation of a tri- or tetra- methoxy or enoxy functional silane crosslinker; water; and, a condensation catalyst selected from the group consisting of stannous carboxylate compounds, dimethyl tin (IV) compounds and mixtures thereof, the water being present in a first of said two parts and said first part further comprising said silanol terminated polyorganosiloxane and the second of said two parts being free of water and comprising said crosslinker component, said condensation catalyst and a tri-methylsilyl terminated polyorganosiloxane, the composition further comprising one or more fillers, and the stoichiometry of the formulation is adjusted to provide a mix ratio of the two parts of 2:1-1:1. ### Claim 6 (depends on 1) A formulation as in claim 1 having an ambient temperature deep section cure time of less than 20 minutes. ### Claim 7 (depends on 1) A formulation as in claim 1 providing a compression set between two mated parts of less than 60% after 1 hour cure at 25.degree. C. prior to compression. ### Claim 8 (depends on 7) A formulation as in claim 7 wherein the compression set is less than 60% after 20 minute cure at 25 .degree. C. prior to compression. ### Claim 9 A fast curing two-part RTV silicone formulation, the first part comprising a silanol terminated polyorganosiloxane having a viscosity in the range of about 1000 cst to 50,000 cst; water; and a filler, and the second part comprising at least 5% by weight of the total formulation of a tri- or tetra- methoxy or enoxy functional silane crosslinker; an effective amount of a condensation catalyst selected from the group consisting of stannous carboxylate compounds, dimethyl tin (IV) compounds and mixtures thereof; and a tri-methylsilyl terminated polyorganosiloxane having a viscosity in the range of about 100 cst to about 10,000 cst. ### Claim 10 (depends on 9) A formulation as in claim 9 wherein the second part comprises at least one dry filler. ### Claim 11 (depends on 9) A formulation as in claim 9 wherein the crosslinker is a tri- or tetra-methoxy functional silane. ### Claim 12 (depends on 9) A formulation as in claim 9 wherein the crosslinker is a tri- or tetra- enoxy functional silane. ### Claim 13 (depends on 9) A formulation as in claim 9 wherein the crosslinker is selected from the group consisting of vinyltrimethoxysilane, methyltrimethoxysilane, phenyltrimethoxysilane, tetramethoxysilane vinyltriisopropenoxysilane, methyltriisopropenoxysilane, phenyltriisopropenoxysilane and tetraisopropenoxysilane. ### Claim 14 (depends on 1) A formulation as in claim 1 wherein the crosslinker is selected from the group consisting of vinyltrimethoxysilane, methyltrimethoxysilane, phenyltrimethoxysilane, vinyltriisopropenoxysilane, methyltriisopropenoxysilane and phenyltriisopropenoxysilane. ### Claim 15 (depends on 7) A formulation as in claim 7 wherein the crosslinker is a trimethoxy functional silane.