# US 5,346,767 A · Abrasion resistant highly filled polyester compositions

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 5,346,767 A
- Document ID: US5346767A
- Status: Granted
- Kind: A
- Application number: 07/994,795
- Filed: 1992-12-22
- Granted: 1994-09-13
- Earliest claimed: 1992-12-22
- Assignees: General Electric Company
- Inventors: Mark G. Tilley; Robert R. Gallucci
- Web page: https://patentgrep.com/patent/US5346767A

## CPC

- C08L 67/02: Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence)
- C08J 7/0427: {with only one layer of a composition containing a polymer binder (with more layers C08J7/042)}
- C08J 7/043: Improving the adhesiveness of the coatings per se, e.g. forming primers (adhesives in the form of films or foils characterised by the primer layers between the polymer carriers and the adhesives C09J7/50)
- C08J 7/046: Forming abrasion-resistant coatings; Forming surface-hardening coatings
- C09D 4/00: Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond {; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16}
- C08J 2367/02: Polyesters derived from dicarboxylic acids and dihydroxy compounds; (C08J2367/06 takes precedence)
- C08J 2433/00: Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Derivatives of such polymers
- C08L 51/04: grafted on to rubbers
- C08L 53/02: of vinyl-aromatic monomers and conjugated dienes
- C08L 67/025: {containing polyether sequences}
- C08L 69/00: Compositions of polycarbonates; Compositions of derivatives of polycarbonates
- C08L 79/08: Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
- Y10T 428/31507: Of polycarbonate
- Y10T 428/31786: Of polyester [e.g., alkyd, etc.]
- Y10T 428/31942: Of aldehyde or ketone condensation product
- C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06)
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)
- C09D: COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR (cosmetics A61K; processes for applying liquids or other fluent materials to surfaces, in general, B05D; staining wood B27K5/02; glazes or vitreous enamels C03C; natural resins, French polish, drying-oils, driers, turpentine, per se, C09F; polishing compositions other than French polish, ski waxes C09G; adhesives or use of materials as adhesives C09J; materials for sealing or packing joints or covers C09K3/10; materials for stopping leaks C09K3/12; processes for the electrolytic or electrophoretic production of coatings C25D)
- Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION

## Abstract

A method of coating is disclosed which is based on applying a composition which is based on colloidal silica dispersed in a silanol or methacrylic derived polymer system or an aminoplast resin to an article of a polybutylene terepthalate or polyethylene terephthalate, or blends of polybutylene terephthalate and polyethylene terephthalate, which optionally include a polycarbonate, or optionally include a polyether ester or polyetherimide ester and a heavy inorganic filler.

## Claims

### Claim 1

A method of coating a composition which comprises:
(a) from 0-70 weight percent of a polybutylene terephthalate resin;
(b) from 0-70 weight percent of a polyethylene terephthalate resin, with the proviso that the sum of the amounts of the polybutylene terephthalate resin and the polyethylene terephthalate resin must be at least 10 weight percent of the total composition;
(c) from 0-35 weight percent of an aromatic polycarbonate resin wherein the resin of (a)+(b) is equal to or greater than (c);
(d) an effective stabilizing amount of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof, phosphates of Group IB and Group IIB metals, and phosphorous oxo-acids;
(e) from 0-15 weight percent of a styrene-rubber impact modifier;
(f) from 0-35 weight percent of a polyetherester or polyetherimide ester resin;
(g) from 30-80 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide, zinc oxide and zinc sulfate; and
(h) from 0-30 percent of a fibrous glass reinforcing filler, said method comprising applying to said composition a curable transparent coating selected from the group consisting of:
(a) a coating comprising a colloidal silica which is dispersed in a silanol, acrylic, methacrylic derived polymer system or mixture thereof; and
(b) a coating comprising an aminoplast resin and thereafter curing said curable transparent coating composition under conditions which will cure said transparent coating.

### Claim 2 (depends on 1)

A method as defined in claim 1 wherein the curable transparent coating is selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 3 (depends on 2)

A method as defined in claim 2 wherein the coating composition is the coating composition of subpart (A).

### Claim 4 (depends on 2)

A method as defined in claim 2 wherein the coating composition is the coating composition of subpart (B).

### Claim 5 (depends on 2)

A method as defined in claim 2 wherein the coating composition is the coating composition of subpart (C).

### Claim 6 (depends on 2)

A method as diefined in claim 2 wherein the coating composition is the coating composition of subpart (D).

### Claim 7 (depends on 1)

The method of claim 1, wherein said inorganic filler is barium sulfate.

### Claim 8 (depends on 1)

A method as defined in claim 1 wherein said method comprises coating an article formed from a composition comprising:
(a) from 7-15 weight percent of polybutylene terephthalate;
(b) from 3-10 weight percent of a polyethylene terephthalate;
(c) from 10-25 weight percent of an aromatic polycarbonate resin;
(d) from 0.01-10 weight percent of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof; phosphates of a Group IB or a Group IIB metal and phosphorous oxo-acids;
(e) from 0-15 weight percent of an styrene rubber impact modifier, and
(f) from 40-79.99 weight percent of an inorganic filler selected from the group consisting of barium sulfate, zirconium oxide, strontium sulfate and zinc sulfate, with a curable coating composition selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 9 (depends on 8)

A method as defined in claim 8 wherein the coating composition is the coating composition of subpart (A).

### Claim 10 (depends on 8)

A method as defined in claim 8 wherein the coating composition is the coating composition of subpart (B).

### Claim 11 (depends on 8)

A method as defined in claim 8 wherein the coating composition is the coating composition of subpart (C).

### Claim 12 (depends on 8)

A method as defined in claim 8 wherein the coating composition is the coating composition of subpart (D).

### Claim 13 (depends on 8)

A method as defined in claim 8 herein the stabilizer is selected from the group consisting of acidic phosphate compounds; phosphites of the formula: ##STR11## wherein R.sup.1, R.sup.2 R.sup.3 are independently selected from the group consisting of hydrogen, alkyl and aryl with the proviso that at least one of R.sup.1, R.sup.2 and R.sup.3 is hydrogen or alkyl; polyacid pyrophosphates of the formula:
M.sub.x.sup.z H.sub.y P.sub.n O.sub.3n+1
wherein M is a metal, x is a number from 1-12 and y is a number from 2-10; z is a number from 1-5 and the sum of (xz)+y=n+2; phosphorous oxo-acids and phosphates of Group IB or Group IIB metals and mixtures thereof.

### Claim 14 (depends on 1)

A process as defined in claim 1 wherein the composition contains 5-30 weight percent of a fibrous glass reinforcing filler.

### Claim 15 (depends on 14)

An article which is made by the process of claim 14.

### Claim 16 (depends on 1)

An article which is made by the process of claim 1.

### Claim 17 (depends on 8)

An article which is made by the process of claim 8.

### Claim 18

A method of coating a composition which comprises:
(a) from 0-30 weight percent of a polybutylene terephthalate resin;
(b) from 0-30 weight percent of a polyethylene terephthalate resin, with the proviso that the sum of the amounts of the polybutylene terephthalate resin and the polyethylene terephthalate resin must be at least 10 weight percent of the total composition;
(c) from 10-30 weight percent of an aromatic polycarbonate resin;
(d) an effective stabilizing amount of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof, phosphate salts of Group IB or Group IIB metals and phosphorous oxo-acids;
(e) from 0-10 weight percent of a styrene-rubber impact modifier;
(f) from 30-79.99 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide and zinc sulfate; and
(g) from 0-30 percent of a fibrous glass reinforcing filler;
said method comprising applying to said composition a curable transparent coating selected from the group consisting of:
(a) a coating comprising a colloidal silica which is dispersed in a silanol, acrylic, methacrylic derived polymer system or mixture thereof; and
(b) a coating comprising an aminoplast resin and thereafter curing said curable transparent coating composition under conditions which will cure said transparent coating.

### Claim 19 (depends on 18)

A method as defined in claim 18 wherein the curable transparent coating is selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 20 (depends on 19)

A method as defined in claim 19 wherein the coating composition is the coating composition of subpart (A).

### Claim 21 (depends on 8)

A method as defined in claim 8 wherein the coating composition is the coating composition of subpart (B).

### Claim 22 (depends on 19)

A method as defined in claim 19 wherein the coating composition is the coating composition of subpart (C).

### Claim 23 (depends on 19)

A method as defined in claim 19 wherein the coating composition is the coating composition of subpart (D).

### Claim 24 (depends on 18)

An article which is made by the process of claim 18.

### Claim 25

A method of coating a composition of a article formed from a composition which comprises:
(a) from 6-10 weight percent polybutylene terephthalate;
(b) from 5-10 weight percent of a polyethylene terephthalate;
(c) from 12-20 weight percent of an aromatic polycarbonate wherein in said molding composition, the ratio of polybutylene terephthalate to polyethylene terephthalate to aromatic polycarbonate is about 2:1:3;
(d) from 0.01-5 weight percent of a stabilizer;
(e) from 1-10 weight percent of a styrene-rubber impact modifier; and
(f) from 59-72.99 weight percent of barium sulfate,
said method comprising applying to said article a curable composition selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 26 (depends on 25)

A method as defined in claim 25 wherein the coating composition is the coating composition of subpart (A).

### Claim 27 (depends on 25)

A method as defined in claim 25 wherein the coating composition is the coating composition of subpart (B).

### Claim 28 (depends on 25)

A method as defined in claim 25 wherein the coating composition is the coating composition of subpart (C).

### Claim 29 (depends on 25)

A method as diefined in claim 25 wherein the coating composition is the coating composition of subpart (D).

### Claim 30 (depends on 25)

A method as defined in claim 25 wherein the stabilizer is an acid phosphate compound.

### Claim 31 (depends on 25)

A method as defined in claim 25 wherein the stabilizer is selected from the group consisting of phosphites of the formula: ##STR12## wherein R.sup.1 R.sup.2 and R.sup.3 are independently selected from the group consisting of hydrogen, alkyl, and aryl with the proviso that at least one of R.sup.1, R.sup.2 and R.sup.3 is hydrogen or alkyl; phosphate salts of a Group IB or Group IIB metal and polyacid pyrophosphates of the formula:
M.sub.x.sup.z H.sub.y P.sub.n O.sub.3n+1
wherein M is a metal, x is a number from 1-12 and y is a number from 2-10; z is a number from 1-5 and the sum of (xz)+y=n+2; and phosphorous oxo-acids.

### Claim 32 (depends on 25)

An article which is made by the process of claim 25.

### Claim 33

A method of coating an article formed from a composition which comprises:
(a) polybutylene terephthalate 0-70 weight percent;
(b) polyethylene terephthalate 0-70 weight percent;
(c) polyether ester or polyetherimide ester 0-35 weight percent; with the proviso that the weight of (a)+(b) is at least equal to or greater than (c) and that the weight of (a)+(b) is at least 10% by weight of total composition;
(d) from 30-80 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide, zinc oxide and zinc sulfate; and
(e) from 0-30 percent of a fibrous glass reinforcing filler,
said method comprising applying to said composition a curable transparent coating selected from the group consisting of:
(a) a coating comprising a colloidal silica which is dispersed in a silanol, acrylic, methacrylic derived polymer system, or mixture thereof; or
(b) a coating comprising an aminoplast resin; and thereafter curing said curable transparent coating under conditions which will cure said transparent coating.

### Claim 34 (depends on 33)

A method as defined in claim 33 wherein the curable transparent coating is selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 35 (depends on 33)

A method as defined in claim 33 wherein the coating composition is the coating composition of subpart (A).

### Claim 36 (depends on 33)

A method as defined in claim 33 wherein the coating composition is the coating composition of subpart (B).

### Claim 37 (depends on 33)

A method as defined in claim 33 wherein the coating composition is the coating composition of subpart (C).

### Claim 38 (depends on 33)

An article which is made by the process of claim 33.

### Claim 39

A method of coating a article formed from a composition which comprises:
(a) polybutylene terephthalate 15-30 weight percent;
(b) polyethylene terephthalate 5-15 weight percent;
(c) polyether ester or polyetherimide ester 5-15 weight percent;
(d) barium sulfate 40-75 weight percent; said method comprising applying to said article a coating composition selected from the group consisting of:
(A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
(B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
(C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica; 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a photoinitiator; or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica; 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane; 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator; and
(D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175; and thereafter curing said coating under curing conditions.

### Claim 40 (depends on 39)

A method as defined in claim 39 wherein the coating composition is the coating composition of subpart (A).

### Claim 41 (depends on 39)

A method as defined in claim 39 wherein the coating composition is the coating composition of subpart (B).

### Claim 42 (depends on 39)

A method as defined in claim 39 wherein the coating composition is the coating composition of subpart (C).

### Claim 43 (depends on 39)

A method as defined in claim 39 wherein the coating composition is the coating composition of subpart (D).

### Claim 44

An abrasion resistant coating for highly filled polyester-containing compositions with suitable adherence thereto, comprising:
(a) from 0-70 weight percent of a polybutylene terephthalate resin;
(b) from 0.14 70 weight percent of a polyethylene terephthalate resin, with the proviso that the sum of the amounts of the polybutylene terephthalate resin and the polyethylene terephthalate resin must be at least 10 weight percent of the total composition;
(c) from 0-35 weight percent of an aromatic polycarbonate resin wherein the resin of (a)+(b) is equal to or greater than (c);
(d) an effective stabilizing amount of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof, phosphates of Group IB or Group IIB metals, and phosphorus oxo-acids;
(e) from 0-15 weight percent of a styrene-rubber impact modifier;
(f) from 0-35 weight percent of a polyetherester or polyetherimide ester resin;
(g) from 30-80 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide, zinc oxide and zinc sulfate; and
(h) from 0-30 percent of a fibrous glass reinforcing filler;
(i) a curable transparent coating selected from the group consisting of
a coating comprising a colloidal silica which is dispersed in a silanol and/or acrylic or methacrylic derived polymer system; and
a coating comprising an aminoplast resin.