# US 5,346,608 A · Method for obtaining neodymium or neodymium-iron alloy by electrolysis of melts containing neodymium compounds > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,346,608 A - Document ID: US5346608A - Status: Granted - Kind: A - Application number: 07/992,691 - Filed: 1992-12-18 - Granted: 1994-09-13 - Earliest claimed: 1991-12-20 - Assignees: Heraeus Elektrochemie GmbH; Moltech Invent S.A. - Inventors: Ulrich Stroder; Jean-Jacques Duruz; Jean-Louis Jorda - Web page: https://patentgrep.com/patent/US5346608A ## CPC - C25C 3/34: of metals not provided for in groups C25C3/02 - C25C3/32 - C25C: PROCESSES FOR THE ELECTROLYTIC PRODUCTION, RECOVERY OR REFINING OF METALS; APPARATUS THEREFOR ## Abstract Neodymium and neodymium-iron alloys are obtained by electrolysis of a neodymium salt melt using magnetite as the anode material. The cathode is non-consumable or is made of iron to be consumed and form a neodymium-iron alloy. The electrolysis is preferably carried out under a protective atmosphere. ## Claims ### Claim 1 In a method for obtaining neodymium or neodymium-iron alloy by electrolysis of a melt containing neodymium oxide, neodymium fluoride, alkali metal fluorides, and optionally alkali earth metal fluorides, using at least one anode and at least one cathode at least partially immersed in the melt, the improvement wherein the anode is a hollow body formed of magnetite and the electrolysis is carried out at a melt temperature from about 750.degree. C. to about 1100.degree. C. ### Claim 2 (depends on 1) A method according to claim 1, wherein said electrolysis is carried out under a protective gas. ### Claim 3 (depends on 1) The method according to claim 1, wherein said hollow body is formed of porous magnetite. ### Claim 4 (depends on 3) The method according to claim 3, further comprising the step of introducing a protective gas into said hollow body under pressure to force it out through the porous magnetite. ### Claim 5 (depends on 1) The method according to claim 1, wherein said hollow body is formed of dense, substantially pore-free magnetite. ### Claim 6 (depends on 5) The method according to claim 5, further comprising the step of generating an underpressure or partial vacuum condition in said hollow body. ### Claim 7 (depends on 5) The method according to claim 5, further comprising the step of generating an overpressure of protective gas in said hollow body. ### Claim 8 (depends on 1) The method according to claim 1, wherein said cathode is of a metal selected from the group consisting of tungsten and molybdenum, and neodymium is recovered. ### Claim 9 (depends on 1) The method according to claim 1, wherein said cathode is an iron cathode, and a neodymium-iron alloy is obtained. ### Claim 10 (depends on 1) The method according to claim 1, wherein a melt of 2-5 weight-% neodymium oxide, 35-92 weight-% neodymium fluoride, 6-60 weight-% lithium fluoride, 0-40 weight-% barium fluoride, and 0-20 weight-% calcium fluoride, is electrolyzed. ### Claim 11 (depends on 10) The method according to claim 10, wherein a melt of 2-4 weight-% neodymium oxide, 78-90 weight-% neodymium fluoride, and 8-20 weight-% lithium fluoride, is electrolyzed. ### Claim 12 (depends on 11) A method according to claim 11, wherein a melt of 2 weight-% neodymium oxide, 80 weight-% neodymium fluoride, and 18 weight-% lithium fluoride, is electrolyzed. ### Claim 13 (depends on 10) The method according to claim 10, wherein said cathode is of a metal selected from the group consisting of tungsten and molybdenum and neodymium is obtained. ### Claim 14 (depends on 10) The method according to claim 10, wherein said cathode is an iron cathode and a neodymium-iron alloy is obtained. ### Claim 15 (depends on 1) The method according to claim 1, wherein a melt of 2-5 weight-% neodymium oxide, 35-92 weight-% neodymium fluoride, 6-60 weight-% lithium fluoride, 0-40 weight-% barium fluoride, and 0-20 weight-% calcium fluoride, is electrolyzed; and said cathode is of a metal selected from the group consisting of tungsten and molybdenum, and neodymium is recovered. ### Claim 16 (depends on 1) The method according to claim 1, wherein a melt of 2-5 weight-% neodymium oxide, 35-92 weight-% neodymium fluoride, and 6-60 weight-% lithium fluoride, 0-40 weight-% barium fluoride, and 0-20 weight-% calcium fluoride, is electrolyzed; and said cathode is an iron cathode, and a neodymium-iron alloy is recovered.