# US 5,344,805 A · Platinum and tin-containing catalyst and use thereof in alkane dehydrogenation

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 5,344,805 A
- Document ID: US5344805A
- Status: Granted
- Kind: A
- Application number: 08/055,343
- Filed: 1993-05-03
- Granted: 1994-09-06
- Earliest claimed: 1993-05-03
- Assignees: Phillips Petroleum Company
- Inventors: Gyanesh P. Khare; Randall A. Porter
- Web page: https://patentgrep.com/patent/US5344805A

## CPC

- B01J 37/0203: {the impregnation liquid containing organic compounds}
- B01J 23/626: {with tin}
- Y02P 20/52: using catalysts, e.g. selective catalysts
- B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- Y02P: CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS

## Abstract

In a process for preparing a dehydrogenation catalyst of the type in which a support comprising zinc aluminate is impregnated with at least one of platinum and tin from an impregnation solution, the improvement comprises simultaneously impregnating the support with the platinum and the tin by contacting the support with an impregnation solution which comprises, in solution, a tin compound, a platinum compound, and a carboxylic acid. The thus prepared catalyst can be employed in the dehydrogenation of at least one alkane containing 2-8 carbon atoms per molecule in the presence of steam.

## Claims

### Claim 1

In a process for preparing a dehydrogenation catalyst comprising the step of impregnating a support comprising zinc aluminate with platinum and tin from an impregnation solution, the improvement which comprises contacting the support with an impregnation solution which has been formed by combining a first solution consisting essentially of water, a platinum compound and oxalic acid and a second solution consisting essentially of water, a tin compound and an inorganic acid.

### Claim 2 (depends on 1)

A process as recited in claim 1 wherein the inorganic acid is hydrochloric acid.

### Claim 3 (depends on 1)

A process as recited in claim 1 wherein the platinum compound is chloroplatinic acid and the tin compound is stannous chloride.

### Claim 4 (depends on 1)

A process as recited in claim 1 wherein platinum of the platinum compound, tin of the tin compound, oxalic acid, and the inorganic acid are present in said impregnating solution in the following weight percentages as based on the weight of the support: about 0.05-5 weight percent of platinum; about 0.1-5 weight percent of tin; about 1-30 weight percent of oxalic acid; and about 0.1-10 weight percent of the inorganic acid.

### Claim 5 (depends on 4)

A process as recited in claim 4 wherein the support further comprises calcium aluminate.

### Claim 6 (depends on 1)

A dehydrogenation catalyst produced in accordance with claim 1.

### Claim 7 (depends on 4)

A dehydrogenation catalyst produced in accordance with claim 4.

### Claim 8 (depends on 5)

A dehydrogenation catalyst produced in accordance with claim 5.

### Claim 9 (depends on 1)

A process in accordance with claim 1 comprising the additional steps of drying the support which has been contacted with said impregnating solution, and calcining the thus-obtained dried, impregnated support in an oxygen-containing atmosphere at a temperature of about 400.degree.-600.degree. C.

### Claim 10 (depends on 9)

A process in accordance with claim 9 wherein said drying is carried out at a temperature of about 80.degree.-250.degree. C.

### Claim 11 (depends on 9)

A process in accordance with claim 9 further comprising the steps of washing the calcined, impregnated support obtained by the process of claim 9 with water so as to remove chloride ions therefrom, and then drying the thus-obtained washed catalyst material.

### Claim 12 (depends on 5)

A process in accordance with claim 5, wherein said dehydrogenation catalyst contains about 80-98 weight percent zinc aluminate, about 0.05-5 weight percent platinum, about 0.1-5 weight percent tin, and about 1-20 weight percent calcium aluminate.

### Claim 13 (depends on 12)

A dehydrogenation catalyst produced in accordance with claim 12.