# US 5,344,605 A · Method of degassing and solidifying an aluminum alloy powder > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,344,605 A - Document ID: US5344605A - Status: Granted - Kind: A - Application number: 07/094,062 - Filed: 1993-09-21 - Granted: 1994-09-06 - Earliest claimed: 1991-11-22 - Assignees: Sumitomo Electric Industries, Ltd. - Inventors: Toshihiko Kaji; Yoshinobu Takeda; Yuusuke Odani; Kiyoaki Akechi; Takao Tanji - Web page: https://patentgrep.com/patent/US5344605A ## CPC - B22F 3/105: by using electric current {other than for infrared radiant energy}, laser radiation or plasma (B22F3/11 takes precedence){; by ultrasonic bonding (B22F3/115 takes precedence)} - B22F 3/1017: {Multiple heating or additional steps (B22F3/101 takes precedence)} - B22F: WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER (making alloys by powder metallurgy C22C); APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER ## Abstract The object is to provide a method of degassing or solidifying an aluminum alloy powder by utilizing an induction heating as a degassing means in a step of forming and solidifying an aluminum powder or aluminum alloy powder, whereby the disadvantages of the prior art can be overcome. The feature of the present invention consists in preforming an aluminum powder, aluminum alloy powder or aluminum composite alloy powder or mixed powders thereof with non-metallic grains to give a specific electric resistance of at most 0.2.OMEGA.cm, subjecting the preform directly to induction heating in an atmosphere at normal pressure, temperature-raising to 400.degree. to 600.degree. C. at a temperature gradient of at least 0.4.degree. C./sec in a temperature range of at least 300.degree. C. and removing heat-decomposable volatile components to obtain a hydrogen content of at most 10 ppm. ## Claims ### Claim 1 A method of degassing an aluminum alloy powder, characterized by preforming an aluminum powder, aluminum alloy powder or aluminum composite alloy powder or mixed powders thereof with non-metallic grains to give a specific electric resistance of at most 0.2.OMEGA.cm, subjecting the preform directly to induction heating in an atmosphere at normal pressure, temperature-raising to 400.degree. to 600.degree. C. at a temperature gradient of at least 0.4.degree. C./sec in a temperature range of at least 300.degree. C., and removing heat-decomposable volatile components to obtain a hydrogen content of at most 10 ppm. ### Claim 2 (depends on 1) The method of degassing an aluminum alloy powder, as claimed in claim 1, wherein the induction heating is carried out in the air. ### Claim 3 (depends on 1, 2) The method of degassing an aluminum alloy powder, as claimed in claim 1 or claim 2, wherein after degassing by the induction heating, the preform is cooled in an inert gas atmosphere. ### Claim 4 A method of solidifying a rapidly solidified aluminum alloy powder, characterized by preforming an aluminum powder, aluminum alloy powder or aluminum composite alloy powder or mixed powders thereof with non-metallic grains to give a specific electric resistance of at most 0.2 .OMEGA.cm, subjecting the preform directly to induction heating in a stagnant atmosphere at normal pressure, maintaining a temperature-raising gradient of at least 0.4.degree. C./sec at a temperature range of at least 300.degree. C., temperature-raising to 400.degree. to 600.degree. C. corresponding to a temperature of at least 30.degree. C. higher than the vacuum degassing temperature applied to a case of extruding the above described powder, removing heat-decomposable volatile components to obtain a hydrogen content of at most 10 ppm, then directly subjecting a product to hot working and solidifying the product. ### Claim 5 (depends on 4) The method of solidifying a rapidly solidified aluminum alloy powder, as claimed in claim 4, wherein the temperature raised by the induction heating is in the range of 400.degree. C. to the melting point. ### Claim 6 (depends on 4, 5) The method of solidifying a rapidly solidified aluminum alloy powder, as claimed in claim 4 or claim 5, wherein the hot working is a powder forging. ### Claim 7 (depends on 4) The method of solidifying a quenched aluminum alloy powder, as claimed in claim 4, wherein the induction heating is carried out in the stagnant atmosphere. ### Claim 8 (depends on 4, 5) The method of solidifying a rapidly solidified aluminum alloy powder, as claimed in claim 4 or claim 5, wherein immediately after forging, the product is quenched at a rate of at least 10.degree. C./sec or reheated at a temperature of at most the forging temperature to at least (the forging temperature -50.degree. C.) without cooling to room temperature, thus effecting quenching and solution treatment. ### Claim 9 (depends on 4, 5, 6) The method of solidifying a rapidly solidified aluminum alloy powder, as claimed in any one of claims 4 to 6, wherein the preforming of the powder is carried out by coating an inner wall of a forming metallic mold with a wetting agent without adding an organic wetting agent to the powder. ### Claim 10 (depends on 4, 5, 6, 7) The method of solidifying a rapidly solidified aluminum alloy powder, as claimed in any one of claims 4 to 7, wherein a radiation heating or direct electric heating is used instead of the induction heating.