.alpha.-olefin-alkenylsilane copolymer and method for preparing same
AssigneeMitsui Toatsu Chemicals, Inc.
InventorsTadashi Asanuma, Kaoru Kawanishi
Life of this patent
Estimating the term…
Abstract
An .alpha.-olefin-alkenylsilane copolymer having steric regularity in which the side chains in the .alpha.-olefin unit substantially have the steric regularity, the content of alkenylsilane units is from 0.01 to 50% by weight, and the intrinsic viscosity measured in a tetralin solution at 135.degree. C. is 0.01 or higher. A method for preparing the above copolymer comprises the step of copolymerizing an .alpha.-olefin having 3 to 25 carbon atoms with an alkenylsilane in the presence of a catalyst comprising an aluminoxane and a transition metal compound containing a cyclopentadiene group or its derivative as a ligand.
Claims6
A syndiotactic .alpha.-olefin-alkenylsilane copolymer in which among peaks attributable to the side chain methyl or methylene groups directly bonded to the main chain of the copolymer and indicative of isotactic, syndiotactic and atactic configurations of the copolymer the alkyl groups in the side chains of the .alpha.-olefin units have a substantially syndiotactic configuration so that, in the .sup.13 C-NMR spectrum of the copolymer observed in a 1,2,4-trichlorobenzene solution,
- (i) a main peak not attributable to the isotactic structure thereof is positioned on the side of higher magnetic field than is the peak attributable to the isotactic structure, and (ii) the intensity of said main peak is 0.3 or more relative to the sum of the intensities of the total peaks attributable to the side chain methyl or methylene groups directly bonded to the main chain;
- the alkenylsilane is represented by the formula;
- H.sub.2 C.dbd.CH--(CH.sub.2).sub.m SiX.sub.3
- wherein X is a hydrogen atom, a halogen atom or a saturated hydrocarbon residue having from 1 to 20 carbon atoms, and m is an integer of from 0 to 10;
- the content of alkenylsilane units is from 3 to 35% by mol;
- and an intrinsic viscosity measured in a tetralin solution at 135.degree. C. is at least 0.01 dl/g.
A method for preparing a syndiotactic copolymer consisting of 65-97% by mol of an .alpha.-olefin and 3-35% by mol of an alkenylsilane which is represented by the formula:
- H.sub.2 C.dbd.CH--(CH.sub.2).sub.m SiX.sub.3
- wherein X is a hydrogen atom, a halogen atom or a saturated hydrocarbon residue having from 1 to 20 carbon atoms, and m is an integer of from 0 to 10, comprising the steps of copolymerizing the .alpha.-olefin with the alkenylsilane in the presence of a soluble catalyst comprising an aluminoxane and a transition metal compound having two asymmetrical ligands combined mutually which are selected from the group consisting of cyclopentadiene groups and derivatives thereof.