Ceramics composite material and production thereof

A method of making a composite refractory material comprising a matrix of a refractory material with particles of a ceramic material dispersed therein, the composite material having a porosity which does not exceed 12 percent, the dispersed particles occupying from 1.0 percent by volume to 40 percent by volume of the composite refractory material, each dispersed particle comprising an agglomerate of microcrystals which (i) are strongly bonded together, (ii) exhibit a strong thermal expansion anisotropy, and (iii) have a size such that cracks do not form spontaneously within the agglomerates during cooling from a temperature of about 1600.degree. C. to room temperature;

• the ceramic material and the refractory material of the matrix being mutually chemically inert in the temperature range of the use of the composite refractory material;
• said method comprising the steps of
• (a) mixing together a powder of the matrix material, a powder of the polycrystalline ceramic material to be dispersed within the matrix material, and a fugitive binder;
• (b) allowing the mixture to dry;
• (c) granulating the dried powder mixture;
• (d) preforming the granulated powder into at least one billet by die pressing;
• (e) isostatically pressing the die pressed billet or billets to form at least one green billet for sintering;
• (f) heating the at least one green billet at a predetermined rate until a sintering temperature in the range from 1200.degree. C. to 1800.degree. C. is reached;
• (g) holding the at least one green billet at the sintering temperature for a period in the range from 0 to 5 hours;
• and
• (h) cooling the sintered billet or billets to ambient temperature;
• characterised in that
• (i) during the cooling step, the or each sintered billet is either (i) thermally quenched to ambient temperature, the thermal quenching being effected when the sintered billet or billets have a temperature above ambient which is a value in the range of from 50.degree. C. to 1500.degree. C.;
• or
• (ii) given at least one thermal down-quench, the down-quench being of a temperature change in the range of from 50.degree. C. to 1500.degree. C.

A composite refractory material, having a porosity which does not exceed 12 percent, the composite refractory material comprising

• (a) a matrix of a polycrystalline refractory ceramic material, a fraction of from 5 percent to 90 percent by volume of the crystalline grains thereof having a diameter in the range of from 15 micrometers to about 80 micrometers;
• and
• (b) particles of a ceramic material dispersed in the matrix material, the dispersed particles occupying from 1.0 percent by volume to 40 percent by volume of the composite refractory material, each dispersed particle comprising an agglomerate of microcrystals which (i) are strongly bonded together, (ii) exhibit a strong thermal expansion anisotropy, and (iii) have a size such that cracks do not form spontaneously within the agglomerates during cooling from a temperature of about 1600.degree. C. to room temperature;
• the dispersed ceramic material and the refractory material of the matrix being mutually chemically inert in the temperature range of the use of the composite refractory material;
• further characterized in that the matrix material and the dispersed ceramic material are selected from the group consisting of
• (1) mullite as the matrix material and zirconia as the dispersed material;
• (2) silicon nitride as the matrix material and boron nitride as the dispersed material;
• (3) barium titanate as the matrix material and zirconia as the dispersed material;
• (4) silicon carbide as the matrix material and boron nitride as the dispersed material;
• (5) alumina as the matrix material and aluminum titanate as the dispersed material;
• (6) spinel as the matrix material and zirconia as the dispersed material;
• and
• (7) fosterite as the matrix material and zirconia as the dispersed material.