Production of foam boards of high compressive strength using a blowing agent mixture
AssigneeBASF SE
InventorsHeinz Voelker, Gerhard Alicke, Manfred Weilbacher, Manfred Weilbacher, Reinhold Weber, Horst Schuch
Life of this patent
Estimating the term…
Abstract
Foam boards of high compressive strength are produced by extruding a mixture of a styrene polymer and from 5 to 16% by weight of a blowing agent which contains a) from 3 to 70% by weight of an alcohol or ketone having a boiling point of from 56.degree. to 100.degree. C., b) from 0 to 50% by weight of carbon dioxide, c) from 0 to 88% by weight of a saturated C.sub.3 - to C.sub.5 -hydrocarbon, d) from 2 to 90% by weight of at least one fluorinated hydrocarbon which has a boiling point of from -30 .degree. to +30.degree. C.
Claims2
A process for the production of foam boards of high compressive strength which have a cross-section of at least 100 CM.sup.2, which comprises extruding a mixture consisting essentially of (1) a polymer component consisting essentially of a styrene polymer, and (2) and 5 to 16% by weight, based on the styrene polymer, of a blowing agent consisting essentially of, based on the weight of the blowing agent:
- a) from 3 to 70% by weight of ethanol,
- b) from 10 to 40% by weight of carbon dioxide,
- c) from 0 to 88% by weight of a saturated C.sub.3 - to C.sub.5 -hydrocarbon, and
- d) from 2 to 90% by weight of at least one fluorinated hydrocarbon selected from the group consisting of difluoroethane, trifluoroethane, tetrafluoroethane and pentafluoroethane.
A process for the production of foam boards of high compressive strength which have a cross-section of at least 100 CM.sup.2, which comprises extruding a mixture consisting essentially of (1) a polymer component consisting essentially of a styrene polymer, (2) from 5 to 16% by weight, based on the styrene polymer of a blowing agent consisting essentially of, based on the weight of the blowing agent:
- a) from 3 to 70% by weight of ethanol,
- b) from 10 to 40% by weight of carbon dioxide,
- c) from 0 to 88% by weight of a saturated C.sub.3 - to C.sub.5 -hydrocarbon, and
- d) from 2 to 90% by weight of at least one fluorinated hydrocarbon selected from the group consisting of difluoroethane, trifluoroethane, tetrafluoroethane and pentafluoroethane and (3) at least one conventional additive selected from the group consisting of antistatics, stabilizers, dyes, lubricants, fillers, flame proofing agents and nucleating agents.
Dependencies are inferred from the claim text.