Method for the preparation of halide glass articles
AssigneeBritish Telecommunications public limited company
InventorsPaul W. France, Steven F. Carter, John R. Williams
Life of this patent
Estimating the term…
Abstract
Halide glass articles, e.g. rods, tubes and preforms for making fluoride glass fibres, are prepared by melting and/or casting the articles under a low pressure, e.g. 0.01 to 500 mbars and, during the low pressure regime, a gas flow rate of between 0.01 to 100 liters/min (measured at NTP) is maintained. It has been found that subjecting the melts to a low pressure reduces the attenuation of the fibre which eventually results from the melts.
Claims22
Method of preparation of a halide glass article which method comprises:
- preparing a halide glass melt,
- casting the glass melt, and
- treating the melt of halide glass with a flow of gas at a pressure less than atmospheric during the preparation of the melt or during the casting of said melt or during both said preparation and said casting wherein at least 90 mole % of the halide of the said halide glass is fluoride.
A method according to any one of the preceding claims, wherein all of the halide of said halide glass is fluoride.
A method of preparing a fluoride glass fibre which fibre comprises a core of a second fluoride glass surrounded by and in contact with a cladding of a first fluoride glass wherein the refractive index of the second fluoride glass is higher than the refractive index of the first fluoride glass, which method comprises:
- (a) providing the precursors of said first fluoride glass into a first crucible,
- (b) providing the precursors of said second fluoride glass into a second crucible,
- (c) transferring each of said crucibles into a furnace and subjecting both crucibles simultaneously to a melting regime comprising, in the order specified,
- (c1) pre-heating said crucibles in the presence of a dry gas at ambient pressure until any evolution of gas has ceased,
- (c2) heating said crucibles to a temperature above the melting point of the glasses in the presence of a mixture of oxygen and inert gas in a mole ratio 1:0 to 1:100,
- (c3) reducing the temperature to below 500 millibars and maintaining a gas flow of 0.01 to 100 liters/min (as measured at normal temperature and pressure),
- (d) transferring the crucibles to a casting zone and casting said first glass composition as a tube and casting said second glass composition into the bore of the said tube whereby a fibre preform is produced, both of said castings being conducted under a pressure of less than 150 millibars and a flow rate of 0.01 to 100 liters/min (as measured at normal temperature and pressure), and
- (e) drawing the fibre preform into a fibre.
A method of preparing a halide glass fibre which method comprises:
- casting a cladding precursor melt as a tube and thereafter casting a core precursor melt into the bore of said tube, the cladding precursor melt being cast into a mould under a flow of gas at a pressure less than atmospheric pressure,
- the core precursor melt being cast into said bore under a pressure which is lower than the pressure at which the cladding precursor melt was cast to thereby form a preform,
- the core precursor melt being cast while at a second temperature which is lower than a first temperature at which the cladding precursor melt was cast and,
- drawing said preform into a fibre.
A method of preparing a fluoride glass fibre which fibre comprises a core of a second fluoride glass surrounded by and in contact with a cladding of a first fluoride glass wherein the refractive index of the second fluoride glass is higher than the refractive index of the first fluoride glass, which method comprises:
- (a) providing precursors of said first fluoride glass into a first crucible,
- (b) providing precursors of said second fluoride glass into a second crucible,
- (c) transferring each of said crucibles into a furnace and subjecting both crucibles simultaneously to a melting regime comprising, in the order specified,
- (c1) pre-heating said crucibles in the presence of a dry gas at ambient pressure until any evolution of gas substantially ceases,
- (c2) heating said crucibles to a temperature above the melting point of the glasses in the presence of a mixture of oxygen and inert gas in a mole ratio of from 1:0 to 1:100,
- (c3) reducing the temperature by at least 50.degree. C. but not to a temperature below 600.degree. C. and causing a flow of gas through said furnace at a pressure in the range 5-150 millibars,
- (d) transferring the crucibles to a casting zone and,
- (d1) casting said first fluoride glass as a tube wherein said casting includes pouring the melted precursors of said first fluoride glass into a mould at a temperature at which its viscosity is 0.01 to 1000 poise under a pressure of 2-100 millibars,
- (d2) casting said second fluoride glass into the bore of said tube whereby a fibre preform is produced, wherein the pouring of the melted precursors of said first fluoride glass into bore is carried out at a temperature which is at least 20.degree. C. lower than the temperature used in step (d1) and under a pressure in the range of 0.1-2 millibars, and
- (e) drawing the fibre preform into a fibre.
A method of preparing halide glass articles which method comprises:
- preparing a melt of a halide glass and thereafter shaping said melt into a halide glass article,
- at least 90% mole of the halide of said halide glass being fluoride, and
- after said melt has been prepared and before it is shaped into said article, treating said melt with a flow of gas at less than atmospheric pressure.
A method for the preparation of a halide glass article which method comprises:
- simultaneously preparing plural melts of halide glass and thereafter casting said melts to thereby form an article,
- at least 90% mole of the halide of said halide glass being fluoride, and
- performing said casting in the presence of a flow of gas at less than atmospheric pressure.
Dependencies are inferred from the claim text.