Impact strength modifiers for thermoplastic polymers

A toughened composition comprising from about 95 to about 5% by weight of a polyamide and from about 5 to about 95% by weight of a polymer modifier which comprises

• A) from about 80 to about 99 parts by weight of a core-shell impact-property-modifier polymer having
• i) from about 50 to about 90 parts by weight of a rubbery core polymer of conjugated diolefin or alkyl acrylate having 2 to 8 carbon atoms in the alkyl group, or mixture thereof, having a glass-transition temperature below -20.degree. C., and
• ii) from about 10 to about 50 parts by weight of one or more shells of polymer, each shell being different from the core or any adjacent shell, at least one of the shells being a copolymer of
• a) a monomer selected from styrenic monomers, acrylonitrile, methacrylonitrile, or alkyl esters of acrylic or methacrylic acid, the alkyl group having from 1 to 8 carbon atoms with
• b) from about 0.5 to about 25%, based on the total weight of the copolymer, of a first copolymerizable unsaturated carboxylic acid, anhydride or mixture thereof, and
• B) from about 1 to about 20 parts by weight of an additive copolymer consisting essentially of about 5 parts by weight of an alkyl acrylate having from 1 to 8 carbon atoms in the alkyl group, with about 57 parts by weight of methyl methacrylate, and about 38 parts by weight of a second copolymerizable unsaturated carboxylic acid, wherein the Notched Izod of the additive copolymer is about 9 joules/meter, at 23.degree. C. and the tensile modulus of the additive copolymer is about 678,000 psi.