Method of fabricating silicon carbide coatings on graphite surfaces
AssigneeThe United States as represented by the United States Department of Energy
InventorsDominic J. Varacalle, Jr., Herbert Herman, Timothy D. Burchell
Life of this patent
Estimating the term…
Abstract
The vacuum plasma spray process produces well-bonded, dense, stress-free coatings for a variety of materials on a wide range of substrates. The process is used in many industries to provide for the excellent wear, corrosion resistance, and high temperature behavior of the fabricated coatings. In this application, silicon metal is deposited on graphite. This invention discloses the optimum processing parameters for as-sprayed coating qualities. The method also discloses the effect of thermal cycling on silicon samples in an inert helium atmosphere at about 1600.degree.C. which transforms the coating to silicon carbide.
Claims8
A method of forming a silicon carbide coating on a graphite substrate comprising the steps of:
- a. vacuum plasma spraying the graphite substrate with a silicon powder within a vacuum plasma spray chamber thereby forming a silicon coating on the substrate, further comprising:
- i. evacuating a plasma spray gun within the vacuum chamber to a pressure of between 20 and 200 mbar;
- ii. mixing and injecting a gas mixture of about 85% argon and 15% hydrogen within the plasma spray gun;
- iii. generating an electric arc within the plasma spray gun;
- iv. passing the mixture through the electric arc, thereby creating a plasma environment;
- and then
- b. removing the as-sprayed graphite substrate from the vacuum chamber;
- c. heating the as-sprayed graphite substrate and silicon coating in an inert gas atmosphere oven to 1600.degree. C.;
- and then
- d. cooling the oven to ambient temperatures, wherein the 1600.degree. C. temperature causes a conversion of the silicon coating on the substrate to the silicon carbide coating, said silicon carbide coating having a porosity in the range of 0.35 to 1.1%, a Vickers hardness in the range of 902 to 968 HV, and a thickness of over 200 .mu.m.
A method of forming a silicon carbide coating on a graphite substrate comprising the steps of:
- a. vacuum plasma spraying the graphite substrate with a silicon powder within a vacuum plasma spray chamber having a vacuum of between 20 and 200 mbar and having an argon primary gas flow of about 50 liters/minute and a hydrogen secondary gas flow of about 10 liters/minute, thereby forming a silicon coating on the substrate;
- b. removing the sprayed graphite substrate from the vacuum chamber;
- c. heating the sprayed graphite substrate and silicon coating in an inert gas atmosphere oven to 1600.degree. C.;
- and then
- d. cooling the oven to ambient temperatures, wherein the 1600.degree. C. temperature causes a conversion of the silicon coating on the substrate to the nonporous silicon carbide coating, said silicon carbide coating having a porosity in the range of 0.35 to 1.1%, a Vickers hardness in the range of 902 to 968 HV, and a thickness of over 200 .mu.m.
Dependencies are inferred from the claim text.