Polyurethane-epoxy interpenetrating polymer network acoustic damping material
AssigneeThe United States of America as represented by the Secretary of the Navy
InventorsUsman A. Sorathia, William L. Yeager, Timothy L. Dapp
Life of this patent
Estimating the term…
Abstract
Improved acoustic damping materials comprise interpenetrating polymer netks having a soft polymer component and a hard polymer component. The soft polymer component, constituting from 50 to 90 percent by weight of the material, is a polyurethane made by polymerization of a diisocyanate with a polyether glycol, and the hard polymer component is made by polymerization of bisphenol A diglycidyl ether, with boron trichloride amine complex as a curing agent.
Claims13
A process for preparing an improved acoustic damping material consisting of an interpenetrating polymer network of a soft polymer component made of polyurethane and a hard polymer component made of an epoxy polymer, comprising the steps of:
- mixing in a predetermined ratio a soft polymer component and a hard polymer component, wherein the constituents of said soft polymer component comprise an aromatic diisocyanate, a previously dried polyalkylene ether glycol, a chain extender, and a cross-linking agent, said constituents of said soft polymer component having the following ratios in equivalents, said dried polyalkylene ether glycol to said aromatic diisocyanate being from about 0.45:1 to about 0.50:1, said chain extender to said aromatic diisocyanate being from about 0.35:1 to about 0.40:1, and said cross-linking agent to said aromatic diisocyanate being from about 0.05:1 to about 0.06:1, and wherein the constituents of said hard polymer component comprise an epoxy resin and a curing agent, the ratio by weight of said epoxy resin to said curing agent being from about 19:1 to about 21:1, and further wherein the predetermined ratio of said soft polymer component to said hard polymer component is from about 1:1 to about 9:1 by weight;
- and
- curing the mixture for from 12 to 20 hours at from 100 to 120 degrees C.
A process for making an improved acoustic damping material consisting of an interpenetrating polymer network of a soft polymer and a hard polymer, comprising the steps of:
- drying a polyalkylene ether glycol by heating said polyalkylene ether glycol in a vacuum to about 100 to110 degrees C.;
- holding said heated polyalkylene ether glycol at said about 100 to 110 degrees C. in a vacuum for about 1 hour;
- cooling said polyalkylene ether glycol to about 70 degrees C.;
- measuring in a predetermined ratio the components of said soft polymer and the components of said hard polymer, said components of said soft polymer comprising an aromatic diisocyanate, said dried polyalkylene ether glycol, a chain extender and a cross-linking agent, wherein the ratio in equivalents of said components of said soft polymer are as follows, said dried polyalkylene ether glycol to said aromatic diisocyanate is from about 0.45:1 to about 0.50:1, said chain extender to said aromatic diisocyanate is from about 0.35:1 to about 0.40:1, and said cross-linking agent to said aromatic diisocyanate is from about 0.05:1 to about 0.06:1, said components of said hard polymer comprising an epoxy resin and a curing agent, wherein the ratio by weight of said epoxy resin to said curing agent is from about 19:1 to about 21:1, and further wherein the predetermined ratio of said soft polymer components to said hard polymer components is from about 1:1 to about 9:1 by weight;
- in a vacuum, mixing said aromatic diisocyanate and said epoxy resin, both said aromatic diisocyanate and said epoxy resin having been preheated to about 50 degrees C., with said dried polyalkylene ether glycol with agitation of the mixture continuing for about 10 minutes;
- adding said cross-linking agent, said chain extender and said curing agent to said mixture with agitation continuing until the resulting mixture reaches about 75 degrees C.;
- pouring said resulting mixture into a mold;
- letting said resulting mixture cure for about 4 hours at about 110 degrees C.;
- removing said resulting mixture from the mold;
- and
- post-curing said mixture for about 16 hours at about 110 degrees C.
Dependencies are inferred from the claim text.