Steel for making very large pipe molds
AssigneeNational Forge Company
InventorAshok K. Khare
Life of this patent
Estimating the term…
Abstract
A ferritic alloy steel that may be used for making very large pipe molds with high ductility and high toughness for centrifugally casting pipe with an inside diameter that may exceed 40 inches, the steel consisting essentially of from about 0.12% to about 0.18% carbon, about 0.70% to about 0.95% manganese, about 0.008% maximum phosphorous, about 0.008% maximum sulphur, about 0.20% to about 0.35% silicon, about 1.05% to about 1.25% nickel, about 1.85% to about 2.25% chromium, about 0.60% to about 0.75% molybdenum, about 0.03% to about 0.08% vanadium, and balance essentially iron.
Claims4
A ferritic alloy steel generally used for high temperature applications in weight percentage consisting essentially of from about 0.12% to about 0.18% carbon, about 0.70% to about 0.95% manganese, about 0.008% maximum phosphorous, about 0.008% sulphur, about 0.20% to about 0.35% silicon, about 1.05% to about 1.25% nickel, about 1.85% to about 2.25% chromium, about 0.60% to about 0.75% molybdenum, about 0.03% to about 0.08% vanadium, and balance essentially iron.
A pipe mold for centrifugally casting pipe formed from a ferritic alloy steel in weight percentage consisting essentially of from about 0.12% to about 0.18% carbon, about 0.70% to about 0.95% manganese, about 0.008% maximum phosphorous, about 0.008% maximum sulphur, about 0.20% to about 0.35% silicon, about 1.05% to about 1.25% nickel, about 1.85% to about 2.25% chromium, about 0.60% to about 0.75% molybdenum, about 0.03% to about 0.08% vanadium, and balance essentially iron.
Dependencies are inferred from the claim text.