US 5,330,692 AGranted

Process for producing an aluminum nitride sintered product

AssigneeMatsushita Electric Works, Ltd.

InventorsNoboru Hashimoto, Kyoji Tanaka, Susumu Kajita, Hiroyoshi Yoden

Life of this patent

Estimating the term…

Loading patent…

Abstract

An aluminum nitride (AlN) sintered product with a high thermal conductivity of 120 W/m.multidot.k or above can be produced at a relatively low sintering temperature of 1650.degree. C. or below in accordance with the following process of the present invention. That is, an A1N powder having a specific surface in a region of about 3.5 to 8 m.sup.2 /g and an oxygen content between 0.5 to 1.8 wt % is mixed with optimum additive amounts of sintering aids (I) to (III) to obtain a mixture powder. The sintering aid (I) is at least one selected from the group consisting of rare earth oxides and rare earth compounds which are converted to corresponding rare earth oxides by the sintering. The sintering aid (II) is at least one selected from the group consisting of alkaline earth oxides and alkaline earth compounds which are converted to corresponding alkaline earth oxides by the sintering. The sintering aid (III) is at least one selected from the group consisting of LAB.sub.6, NbC, and WB. The optimum additive amount of LaB.sub.6 is in a range of 0.05 to 3 wt % of the A1N sintered product. The mixture powder is compacted, and then sintered at the sintering temperature in a non-oxidation atmosphere to obtain the A1N sintered product.

Claims4

Dependent claims

In a process for producing an aluminum nitride (AlN) sintered product, which comprises the steps of adding sintering aids to AlN powder to form a mixture, compacting the resulting mixture, and then sintering the compacted mixture at a sintering temperature in a non-oxidizing atmosphere;

said AlN powder having a specific surface area in a range of about 3.5 to 8 m.sup.2 /g and an oxygen content between 0.5 and 1.8 wt %;
said sintering aids comprising:
a first sintering aid comprising at least one selected from the group consisting of rare earth oxides and rare earth compounds which are converted to corresponding rare earth oxides by said sintering, said first sintering aid being incorporated such that an equivalent rare earth oxide amount thereof is in a range of 0.5 to 10 wt % in relation to the AlN sintered product;
a second sintering aid comprising at least one selected from the group consisting of alkaline earth oxides and alkaline earth compounds which are converted to corresponding alkaline earth oxides by said sintering, said second sintering aid being incorporated such that an equivalent alkaline earth oxide amount is in a range of 0.1 to 5 wt % in relation to the AlN sintered product;
and
LaB.sub.6 as a third sintering aid, an additive amount of said third sintering aid being in a range of 0.05 to 3 wt % of the AlN sintered product.

3 more elements