Process and apparatus for renewing the refractory lining of foundry ladles
AssigneeIntocast GmbH Feuerfestprodukte und Giesshilfsmittel
InventorWilhelm Eitel
Life of this patent
Estimating the term…
Abstract
A process for renewing the refractory lining of a ladle for casting steel and of similar metallurgical vessels. While the ladle (10) is still hot, the slag (S) still adhering to the inner surface (26) is melted off from the remaining lining (2) with the aid of a high-temperature burner (9) operating under reducing conditions and allowed to run out of the ladle (10) in the molten condition. After cooling, the glassy surface of the remaining lining (2) is roughened. The new refractory lining (30) is then applied by casting, with the aid of a template.
Claims6
A process for renewing a refractory lining of a ladle, the refractory lining having a predetermined thickness, and the ladle containing at least one of:
- 1) a slag which is adhered to the refractory lining, and 2) a slag-impregnated surface layer of the refractory lining, the process comprising the steps of:
- A) heating the ladle;
- B) tilting the ladle on a side thereof such that the ladle is sloped relative to a horizontal plane wherein an opening of the ladle is located proximate a lower end of the sloped ladle;
- C) melting at least one of the slag and the slag-impregnated surface layer via a high-temperature burner that utilizes pure oxygen and allowing the melted at least one of the slag and the slag-impregnated surface layer to run out of the opening so that after melting has ended, the refractory lining has an exposed glassy surface;
- D) cooling the ladle;
- E) roughening the exposed glassy surface;
- then
- F) casting a refractory lining material against the roughened exposed glassy surface to form a renewed refractory lining adhered to the roughened exposed glassy surface of the refractory lining such that a thickness of the renewed refractory lining combined with the refractory lining is approximately the same as the predetermined thickness of the refractory lining.
An apparatus for renewing a refractory lining of a ladle used for casting metallurgical material, the apparatus comprising:
- a stand upon which the ladle is removably supported to lie at an angle relative to a horizontal plane so that an opening of the ladle is located proximate a lower end of the angled ladle;
- a movable high-temperature burner being removably disposed in the ladle and guidable along an inner surface of the ladle, the high-temperature burner being pivotable, rotatable and displaceable along a longitudinal axis of the ladle, the high-temperature burner melting at least one of a slag adhered to the refractory lining and a slag-impregnated surface layer of the refractory lining so that the melted at least one of the slag and the slag-impregnated surface layer exits the ladle via the opening;
- a device which receives the melted at least one of the slag and the slag-impregnated surface layer exiting the opening;
- a roughening device for roughening an exposed glassy surface of the refractory lining which exists after the melted at least one of the slag and the slag-impregnated surface layer has exited via the opening;
- a template lowerable into the ladle such that at times when the template is in the ladle, a space is defined between the template and a portion of the refractory lining which remains after the melted at least one of the slag and the slag-impregnated surface layer exits the opening and the roughening device has roughened the exposed glassy surface;
- and
- a feed device for feeding lining material in the space for renewal of the refractory lining.
A process for renewing a refractory lining of a ladle, the refractory lining having a predetermined thickness, and the ladle containing at least one of:
- 1) a slag which is adhered to the refractory lining, and 2) a slag-impregnated surface layer of the refractory lining, the process comprising the steps of:
- A) heating the ladle;
- then
- B) tilting the ladle on a side thereof such that the ladle is sloped relative to a horizontal plane wherein an opening of the ladle is located proximate a lower end of the angled ladle;
- then
- C) melting at least one of the slag and the slag-impregnated surface layer via a high-temperature burner that utilizes pure oxygen and allowing the melted at least one of the slag and the slag-impregnated surface layer to run out of the opening so that after melting has ended, the refractory lining has an exposed glassy surface;
- then
- D) cooling the ladle;
- then
- E) roughening the exposed glassy surface;
- then
- F) casting a refractory lining material against the roughened exposed glassy surface to form a renewed refractory lining adhered to the roughened exposed glassy surface of the refractory lining.