US 5,328,867 A · Peroxide clean before buried contact polysilicon deposition

Abstract

A method of removing impurities from the surface of an integrated circuit and forming a uniform thin native oxide layer on the same surface of an integrated circuit is described. A hydrofluoric acid solution, followed by a rinse and spin dry, is often used to remove gate oxide from within an opening etched in a polysilicon layer. The rinsing leaves water spots. Spin drying leaves impurities where water tracks were. An H.sub.2 O.sub.2 cleaning is performed to remove the water spots. After the cleaning, a uniform thin layer of native oxide is formed on the surface of the silicon substrate. A second layer of polysilicon is deposited over this first thin native oxide layer and doped with an implant dosage chosen so that it will go through the uniform native oxide layer. The substrate is annealed to drive in the buried contact. Processing continues to form polysilicon or silicide gate electrodes. Source and drain regions are formed within the openings to the silicon substrate between the gate electrodes. Spacers are formed on the sidewalls of the gate electrodes. An insulating layer is deposited over the surface of the silicon substrate. Contact openings are etched through the insulating layer to the second polysilicon layer and to the silicon substrate. A metal layer is deposited over the insulating layer and filling the openings to the second polysilicon layer and the silicon substrate. The metal layer is patterned, completing the formation of the buried contacts within the integrated circuit.

Claims31

Dependent claims

The method of removing water spots from the surface of an integrated circuit comprising:

providing a thin layer of native oxide on the surface of said integrated circuit;
etching away said thin native oxide layer;
rinsing and drying said surface after said etching away of said native oxide layer whereby water spots are formed on the surface of said integrated circuit as a result of said rinsing and drying;
and
H.sub.2 O.sub.2 cleaning of said surface to remove said water spots whereby a uniform second thin layer of native oxide is formed on the surface of said integrated circuit as a result of said H.sub.2 O.sub.2 cleaning process.

2 more elements

The method of fabricating an integrated circuit with buried contacts comprising:

forming a gate oxide layer on a silicon substrate;
depositing a first layer of polysilicon over said gate oxide layer;
patterning said first polysilicon layer to form openings to said gate oxide layer;
etching away said gate oxide layer within said openings;
rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying;
H.sub.2 O.sub.2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H.sub.2 O.sub.2 cleaning process;
depositing a second layer of polysilicon over said first thin native oxide layer;
doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate;
annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer;
etching away said second thin native oxide layer;
rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying;
H.sub.2 O.sub.2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H.sub.2 O.sub.2 cleaning process;
patterning said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate;
forming source and drain regions within openings to said silicon substrate between said gate electrodes;
forming spacers on the sidewalls of said gate electrodes;
depositing an insulating layer over the surface of said silicon substrate;
etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate;
depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate;
and
patterning said metal layer to complete said buried contacts within said integrated circuit.

17 more elements

The method of fabricating an integrated circuit with buried contacts comprising:

forming a gate oxide layer on a silicon substrate;
depositing a first layer of polysilicon over said gate oxide layer;
patterning said first polysilicon layer to form openings to said gate oxide layer;
etching away said gate oxide layer within said openings;
rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying;
H.sub.2 O.sub.2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H.sub.2 O.sub.2 cleaning process;
depositing a second layer of polysilicon over said first thin native oxide layer;
doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate;
annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer;
etching away said second thin native oxide layer;
rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying;
H.sub.2 O.sub.2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H.sub.2 O.sub.2 cleaning process;
etching said silicon substrate to remove said third native oxide layer;
depositing a layer of tungsten silicide on top of said second polysilicon layer;
patterning said tungsten silicide layer and said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate;
forming source and drain regions within openings to said silicon substrate between said gate electrodes;
forming spacers on the sidewalls of said gate electrodes;
depositing an insulating layer over the surface of said silicon substrate;
etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate;
depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate;
and
patterning said metal layer to complete said buried contacts within said integrated circuit.

19 more elements

Dependencies are inferred from the claim text.