AssigneeCorning Incorporated
InventorsWilliam H. Dumbaugh, Jr., Josef C. Lapp
Life of this patent
Estimating the term…
Abstract
This invention is directed to glass compositions particularly designed for use as substrates in flat panel display devices and, more expressly, for use as substrates in LCDs which employ polycrystalline silicon thin film transistors. The glass compositions are essentially free from alkali metal oxides and consist essentially, in mole percent, of ______________________________________ SiO.sub.2 65-76 MgO 0-5 ZrO.sub.2 0-2.5 Al.sub.2 O.sub.3 7-11 CaO 0-10 TiO.sub.2 0-3 BaO 12-19 SrO 0-10 Ta.sub.2 O.sub.5 0-3 B.sub.2 O.sub.3 0-5 MgO + 0-15 ZrO.sub.2 + 0.5-5. CaO + TiO.sub.2 + SrO Ta.sub.2 O.sub.5 ______________________________________
Claims4
A glass exhibiting a strain point higher than 660.degree. C., a liquidus temperature no higher than 1,175.degree. C., a weight loss of less than 1 mg/cm.sup.2 after immersion for 24 hours in an aqueous 5% by weight HCl solution at 95.degree. C., and long term stability against devitrification at melting and forming temperatures, said glass being essentially free from alkali metal oxides and consisting essentially, expressed in terms of mole percent on the oxide basis, of
- ______________________________________ SiO.sub.2 65-76 MgO 0-5 Al.sub.2 O.sub.3 7-11 CaO 0-10 TiO.sub.2 0-3 BaO 12-19 SrO 0-10 Ta.sub.2 O.sub.5 0-3 B.sub.2 O.sub.3 0-5 MgO + 0-15 TiO.sub.2 + 0.5-5. CaO + Ta.sub.2 O.sub.5 SrO ______________________________________
In a liquid crystal display device which employs polycrystalline silicon thin film transistors as switches, which device contains a flat, transparent glass substrate, the improvement wherein said glass exhibits a strain point higher than 660.degree. C., a liquidus temperature no higher than 1,175.degree. C., a weight loss of less than 1 mg/cm.sup.2 after immersion for 24 hours in an aqueous 5% by weight HCl solution at 95.degree. C., and long term stability against devitrification at melting and forming temperatures, said glass being essentially free from alkali metal oxides and consisting essentially, expressed in terms of mole percent on the oxide basis, of
- ______________________________________ SiO.sub.2 65-76 MgO 0-5 Al.sub.2 O.sub.3 7-11 CaO 0-10 TiO.sub.2 0-3 BaO 12-19 SrO 0-10 Ta.sub.2 O.sub.5 0-3 B.sub.2 O.sub.3 0-5 MgO + 0-15 TiO.sub.2 + 0.5-5. CaO + Ta.sub.2 O.sub.5 SrO ______________________________________
Dependencies are inferred from the claim text.