Method for forming attachment surfaces on implants
AssigneeHowmedica, Inc.
InventorKofi B. Kwarteng
Life of this patent
Estimating the term…
Abstract
An improved method of producing a site for tissue ingrowth on a surgical implant by embedding a space occupier possessing a desired pattern in the surface of the implant at the desired location for ingrowth and then solubilizing the embedded space occupier to leave the pattern on the implant surface. Preferably, the implant is fabricated from a composite comprising a semi-crystalline thermoplastic resin such as polyetheretherketone or polyphenylene sulfide, and the space occupier is an acid-soluble metal plate machined to produce the desired pattern and removed by aqueous acid solution. The space occupier is embedded onto the composite surface by induction heating.
Claims6
A method of producing a site for tissue ingrowth on at least a portion of a surface of a compression molded composite surgical implant comprising the steps of:
- placing a metal space occupier possessing a desired tissue ingrowth pattern over the portion of the surface of the molded composite surgical implant;
- placing a release film over the space occupier;
- placing a tightly fitting metal susceptor over the release film in the area of said space occupier;
- clamping said susceptor over said implant in a fixed position with respect thereto with a clamp;
- heating only the surface of said composite implant by heating said metal space occupier by induction heating to a temperature above a melting point of the composite implant in the presence of only a thermal expansion force generated by said heating with said clamp in place to allow the space occupier to become embedded therein;
- and
- solubilizing the embedded space occupier with an agent non-reactive toward the implant to remove the space occupier and leave the desired pattern in the implant surface to accept tissue ingrowth.
A method of producing a site for tissue ingrowth on a compression molded composite surgical implant, said implant having curved surfaces, comprising the steps of:
- placing a metal space occupier possessing a desired tissue ingrowth pattern over at least a portion of the curved surfaces of the composite surgical implant;
- placing a release film over the space occupier;
- placing a tightly fitting metal susceptor over the release film in the area of said space occupier;
- clamping said susceptor over said implant in a fixed position with respect thereto with a clamp;
- heating only the surface of said composite implant by heating said metal space occupier to a temperature above a melting point of the composite implant in the presence of only a thermal expansion force generated by said heating with said clamp in place to allow the space occupier to become embedded therein;
- and
- solubilizing the embedded space occupier with an agent non-reactive toward the implant to remove the space occupier and leave the desired pattern in the implant surface to accept tissue ingrowth.
Dependencies are inferred from the claim text.