US 5,317,008 A · Method of manufacturing bismuth type oxide superconductor

Abstract

A method of manufacturing a bismuth oxide superconductor, wherein a molded body of a bismuth oxide superconducting substance comprising bismuth, an alkaline earth metal, copper, and oxygen or a precursor thereof is subjected to a heat treatment for producing a superconducting phase and then subjected to one step selected from (1) a step of cooling the heated body from 700.degree. C. to 200.degree. C. in an atmosphere having an oxygen partial pressure of not less than 0.1 atm at a cooling rate of not less than 10.degree. C./min, (2) a step of cooling the heated body from 700.degree. C. in an atmosphere having an oxygen partial pressure of less than 0.1 atm at a cooling rate of less than 10.degree. C./min, and (3) a step of cooling the heated body, and then performing a heat treatment for the cooled heated body in an atmosphere having an oxygen partial pressure of not more than 0.1 atm at a temperature from 700.degree. C. to 200.degree. C.

Claims18

Dependent claims

A method of manufacturing a bismuth oxide superconductor comprising:

(i) applying a two-stage heat treatment to a molded body of a substance selected from the group consisting of (a) a bismuth oxide superconducting substance comprising bismuth, an alkaline earth metal, copper and oxygen and (b) a precursor thereof, to produce a superconducting phase, a first stage of the two-stage heat treatment being applied to heat and sinter said molded body at a temperature within a temperature range from a temperature of T.sub.M -20.degree. C. inclusive, T.sub.M being the melting start temperature of said substance which is heated and sintered, to a temperature T.sub.M +40.degree. C. exclusively, and a second stage of the two-stage heat treatment being applied to heat the molded body in an atmosphere having an oxygen partial pressure of not less than 0.2 atm at a temperature from 700.degree. C. to 890.degree. C;
and
(ii) cooling the heated body from 700.degree. C. to 100.degree. C. in an atmosphere having an oxygen partial pressure of not less than 0.2 atm at a cooling rate of not less than 12.degree. C./minute, thereby suppressing the oxygen content of said bismuth oxide superconductor and providing a bismuth oxide superconductor having a high critical temperature and a high critical current density.

A method of manufacturing a bismuth oxide superconductor comprising

(i) applying a two-stage heat treatment to a molded body of a substance selected from the group consisting of (a) a bismuth oxide superconducting substance comprising bismuth, an alkaline earth metal, copper and oxygen and (b) a precursor thereof, to produce a superconducting phase, a first stage of the two-stage heat treatment being applied to heat and sinter said molded body at a temperature within a temperature range from a temperature of T.sub.M -20.degree. C. inclusive, T.sub.M being the melting start temperature of said substance which is heated and sintered, to a temperature T.sub.M +40.degree. C. exclusively, and a second stage of the two-stage heat treatment being applied to heat the molded body in an atmosphere having an oxygen partial pressure of not less than 0.2 atm at a temperature from 700.degree. C. to 890.degree. C.;
and
(ii) cooling the heated body from 700.degree. C. to 100.degree. C. in an atmosphere having an oxygen partial pressure of at most 0.08 atm at a cooling rate of at most 5.degree. C./minute, thereby suppressing the oxygen content of said bismuth oxide superconductor and providing a bismuth oxide superconductor having a high critical temperature and a high critical current density.

A method of manufacturing a bismuth oxide superconductor comprising

(i) applying a two-stage heat treatment to a molded body of a substance selected from the group consisting of (a) a bismuth oxide superconducting substance comprising bismuth, an alkaline earth metal, copper and oxygen and (b) a precursor thereof, to produce a superconducting phase, a first stage of the two-stage heat treatment being applied to heat and sinter said molded body at a temperature within a temperature range from a temperature of T.sub.M -20.degree. C. inclusive, T.sub.M being the melting start temperature of said substance which is heated and sintered, to a temperature T.sub.M +40.degree. C. exclusively, and a second stage of the two-stage heat treatment being applied to heat the molded body in an atmosphere having an oxygen partial pressure of not less than 0.2 atm at a temperature from 700.degree. C. to 890.degree. C.;
and
(ii) cooling the heated body thereby forming a superconductor containing excessive oxygen, followed by heating said superconductor containing excessive oxygen in an atmosphere having an oxygen partial pressure of at most 0.08 atm at a temperature of 120.degree. C. to 650.degree. C. for 3 to 20 hours thereby removing the excessive oxygen from the superconductor, and providing a bismuth oxide superconductor having a high critical temperature and a high critical current density.

Dependencies are inferred from the claim text.

Method of manufacturing bismuth type oxide superconductor

Life of this patent

Method of manufacturing bismuth type oxide superconductor

Life of this patent

Abstract

Claims18