US 5,314,866 A · Formation of superconducting Bi-Sr-Ca-Cu-O films by organometallic chemical vapor deposition

Abstract

A CVD process for forming a layer or layers of superconducting materials on a semiconductor substrate in which volatile organometallic compounds of bismuth, strontium, calcium and copper are heated in the presence of a carrier gas in a first chamber free of hydrolyzing agents. Under conditions free of hydrolyzing agents, the carrier gas transports a predetermined quantity of the volatile organometallic compounds of the bismuth, strontium, calcium and copper to a deposition chamber. The compounds are decomposed and deposit mixed oxides on the substrate. Subsequent to deposition of the mixed oxides of the desired elements the layer is sintered in an oxygen-rich atmosphere, and formed into a superconducting film by subsequent slow cooling still in an oxygen-rich atmosphere.

Claims2

Dependent claims

A method of coating at least one film of a superconductor composition on a substrate comprising the steps of:

(a) providing triphenylbismuth, strontium 2,2,6,6-tetramethyl-3,5-heptanedionate, calcium 2,2,6,6-tetramethyl-3,5-heptanedionate and copper acetylacetonate as organometallic precursors;
(b) flowing a carrier gas free of hydrolyzing agents over said organometallic precursors at a rate sufficient to take up an amount of said organometallic precursors;
(c) transporting said organometallic precursors under conditions free of hydrolyzing agents to a deposition chamber;
(d) mixing oxygen and said organometallic precursors in the deposition chamber to decompose said organometallic precursors and deposit mixed oxides on said substrate;
(e) sintering the mixed oxides at a temperature between about 500.degree. C. and 900.degree. C. to form a coated substrate;
(f) cooling the coated substrate to ambient temperature to produce said substrate coated with at least one said film of said superconductor composition.

3 more elements

Dependencies are inferred from the claim text.

Formation of superconducting Bi-Sr-Ca-Cu-O films by organometallic chemical vapor deposition

Life of this patent

Formation of superconducting Bi-Sr-Ca-Cu-O films by organometallic chemical vapor deposition

Life of this patent

Abstract

Claims2