Method of manufacturing interconnect metallization comprising metal nitride and silicide

In the manufacture of a semiconductor device, a method comprising the steps of:

• providing a semiconductor substrate having an insulation film disposed thereon;
• forming an aperture in the insulation film in order to expose a portion of the semiconductor substrate;
• forming a refractory metal layer on the insulation film and the exposed portion of the substrate, so that the refractory metal layer has an exposed surface;
• depositing a refractory metal nitride layer on the exposed surface of the refractory metal layer above the insulation film and the exposed portion of the substrate, the refractory metal nitride layer having an exposed surface;
• after said steps of forming a refractory metal layer and depositing a refractory metal nitride layer, carrying out a rapid thermal annealing of those layers at a temperature from 600.degree. to 1000.degree. C. and in an atmosphere containing nitrogen and oxygen, said rapid thermal annealing step being performed for changing the refractory metal layer on the exposed surface of the substrate to a refractory metal silicide layer, changing the refractory metal nitride layer above the exposed portion of the substrate to a silicon atom-containing refractory metal nitride layer, and changing the exposed surface of the refractory metal nitride layer to have an oxygen atom-containing refractory metal nitride composition;
• and, after said step of carrying out a rapid thermal annealing, forming an Al or Al alloy body on the oxygen atom-containing surface of the refractory metal nitride layer.