Processable, high molecular weight polyaniline and fibers made therefrom
AssigneeThe Trustees of the University of Pennsylvania
InventorsAlan G. MacDiarmid, Elliot Scherr, Xun Tang
Life of this patent
Estimating the term…
Abstract
Substantially amorphous, high molecular weight polyaniline which is processable into shaped articles such as fibers is disclosed. Polyaniline base made by standard procedures is subjected to extraction to remove impurities and lower molecular weight fractions. The resulting high molecular weight base, which is partially crystalline and insoluble in NMP and concentrated H.sub.2 SO.sub.4, is converted to an amorphous material soluble in NMP and concentrated H.sub.2 SO.sub.4, by a two step process involving conversion to a salt, and reconversion to a base. Fibers prepared from the high molecular weight material exhibit conductivities in the range of about 50 to 100 S/cm.
Claims15
A method of preparing fibers of high molecular weight polyaniline comprising drawing a viscous solution of an amorphous polyaniline base having a molecular weight of at least about 300,000 as determined by gel permeation chromatography into a fiber in a coagulating bath selected from the group consisting of non-solvents for said polyaniline and mixtures of solvents and non-solvents for said polyaniline, and allowing the drawn polyaniline to precipitate.
A method of preparing fibers of high molecular weight polyaniline comprising
- (a) providing partially crystalline polyaniline base;
- (b) substantially converting said polyaniline base to a protonic acid salt;
- (c) substantially reconverting said salt to a base, wherein said reconverted base is an amorphous, high molecular weight polyaniline base having a molecular weight of at least about 300,000 as determined by gel permeation chromatography;
- and
- (d) drawing a viscous solution of the product of step (c) into a fiber in a coagulating bath selected from the group consisting of non-solvents for said polyaniline and mixtures of solvents and non-solvents for said polyaniline, and allowing the drawn polyaniline to precipitate.
Polyaniline fibers prepared from a solution of polyaniline base in NMP which exhibits, upon gas permeation chromatography using a polystyrene standard, two peaks, the major peak having a molecular weight of at least about 300,000.
A method of using an amorphous polyaniline base having a molecular weight of at least about 300,000 as determined by gel permeation chromatography comprising drawing a viscous solution of said polyaniline base into a fiber in a coagulating bath selected from the group consisting of non-solvents for said polyaniline and mixtures of solvents and non-solvents for said polyaniline, and allowing the drawn polyaniline to precipitate.
Dependencies are inferred from the claim text.