Process for forming a coated active agent-containing article
AssigneeDow Corning Corporation
InventorsJohn T. Woodard, Martin C. Musolf, Patrick J. Miller
Life of this patent
Estimating the term…
Abstract
Aqueous coating compositions for forming elastomeric films around active cores (e.g., drugs) comprising a dispersion of pre-crosslinked polyorganosiloxane latex particles, colloidal silica particles, and a water-dispersible organic material (e.g., polyethylene glycol) are disclosed and claimed. The elastomeric films formed by the coating compositions are used to control the rate of release of an active agent in the cores into an aqueous environment. Methods of formulating the coating compositions and active cores coated with the coating compositions are also disclosed.
Claims14
A process for forming an elastomeric coating on an active-agent-containing core for the controlled release of the active agent through the elastomeric coating which comprises the following steps:
- A) preparing a polyorganosiloxane latex, which is free of organometallic catalysts, as follows:
- i) forming a first solution by dissolving 0.5 to 15 parts by weight of one or more alkoxy silicon compounds of the formula R'.sub.a Si(OR").sub.4-a in 100 parts by weight of a liquid hydroxyl endblocked polydiorganosiloxane polymer of the formula HO(R.sub.2 SiO).sub.x H;
- ii) forming a second, aqueous solution by dissolving from 15 to 75 millimoles of an anionic surfactant in approximately 50 to 200 parts by weight of water;
- iii) mixing said first and second solution together to form a homogenous emulsion;
- iv) holding said homogenous emulsion at room temperature and at an acid pH for a period in excess of 5 hours whereby a crosslinked polyorganosiloxane latex is formed;
- and
- v) neutralizing said emulsion with a base, thereby terminating the crosslinking reaction;
- where R is selected from the group consisting of phenyl, vinyl, alkyl, and 3,3,3-trifluoropropyl radicals, R' is a monovalent hydrocarbon radical having up to 12 carbon atoms, R" is an alkyl radical having 1 to 6, inclusive, carbon atoms, x has an average value in the range of from 3 to 100, inclusive, and a is 0 or 1;
- B) blending 100 parts by weight of said crosslinked polyorganosiloxane latex formed in step A hereof with from 5 to 50 parts by weight of colloidal silica particles and 8 to 100 parts by weight of a water-dispersible organic material selected from the group consisting of polyvinylpyrrolldone and polyhydric alcohols and esters thereof, thereby forming an aqueous coating composition;
- C) adjusting the viscosity of said coating composition, as necessary, to a range which permits coating of an active core;
- D) applying said aqueous coating composition to the exterior surfaces of said active core;
- and
- E) evaporating the water on said exterior surfaces of said active core whereby an elastomeric film is formed.
Dependencies are inferred from the claim text.