Process for the increase in critical temperature of high T.sub.c superconductors
AssigneesDuke University, IBM Corporation
InventorsF. Hadley Cocks, Nancy J. Bolinger, Holly M. Hammarstrom
Life of this patent
Estimating the term…
Abstract
A method is disclosed to increase the critical transition temperature of superconducting materials by the selective application of stress to specific crystal directions. It has been found that by applying tensile stresses in certain directions and compressive stresses in other directions that the critical temperature of superconducting materials can be substantially increased.
Claims3
A method for increasing the critical transition temperature of a high temperature superconducting material having three crystal axes, said method comprising the steps of:
- (a) providing the high temperature superconducting material;
- and
- (b) applying nonhydrostatic stressing to said superconducting material by providing tension in the direction of one crystal axis and compression in the direction of at least one of the other two crystal axes.
A method for increasing the critical transition temperature of a high temperature superconducting material having three crystal axes, said method comprising the steps of:
- (a) providing a high temperature superconducting material which exhibits different superconducting transition temperatures at different chemical compositions;
- (b) measuring the lattice parameters exhibited by said high temperature superconducting material as a function of said different chemical compositions;
- (c) measuring said different superconducting transition temperatures at said different chemical compositions;
- (d) calculating the dependence of said superconducting transition temperatures upon said lattice parameters;
- (e) applying compressive strain in those crystal lattice parameter directions which exhibit a negative effect on said transition temperatures;
- and
- (f) applying a tensile strain in those crystal lattice directions which exhibit a positive effect on said transition temperatures whereby said superconducting transition temperatures are increased.
Dependencies are inferred from the claim text.