Fused quartz member for use in semiconductor manufacture
OwnerPeter P. Bihuniak, Gordon E. Dogunke +1inventors
InventorsPeter P. Bihuniak, Gordon E. Dogunke, Robert D. Shelley
Life of this patent
Estimating the term…
Abstract
A composite fused quartz material is disclosed for processing semiconductor grade silicon material in an improved manner. The modified vitreous material includes a disperse phase of fine size silicon metal particles which are distributed in preselected regions of the fused quartz matrix as a means of exercising temperature control in the various semiconductor processing operations using these fused quartz parts. Such utilization of the modified vitreous material in single crystal silicon rod growth and production of semiconductor grade silicon by diffusion doping is described. A method to produce the modified vitreous material is also disclosed.
Claims4
A process for drawing single crystal silicon from a molten polysilicon mass at elevated temperature which comprises the steps of:
- (a) introducing a polysilicon mass into a fused quartz crucible;
- (b) applying heat to said polysilicon mass in said crucible in order to melt said polysilicon mass to a temperature suitable for drawing a silicon single crystal therefrom, at least a portion of said heat being in the form of infrared radiation which passes through at least a portion of said crucible to said polysilicon mass;
- (c) drawing a silicon single crystal from said molten polysilicon mass while maintaining heat to said mass sufficient to keep same in a molten condition;
- and
- (d) reducing the amount of radiant heat passing through into the interior of said crucible at that portion of said crucible above said molten polysilicon mass during said drawing of said silicon single crystal by means of a disperse phase of from about 25 ppm up to about 2000 ppm by weight of fine size, spherically-shaped silicon metal crystals uniformly distributed throughout said fused quartz crucible at that portion thereof above the level of said molten polysilicon mass so as to reduce infrared optical transmission through said portion to a room temperature value no greater than about 30% to a 3 mm sample thickness.
A process for drawing single crystal silicon from a molten polysilicon mass at elevated temperature which comprises the steps of:
- (a) introducing a polysilicon mass into a fused quartz crucible;
- (b) applying heat to said polysilicon mass in said crucible in order to melt said polysilicon mass to a temperature suitable for drawing a silicon single crystal therefrom, at least a portion of said heat being in the form of infrared radiation which passes through at least a portion of said crucible to said polysilicon mass;
- (c) drawing a silicon single crystal from said molten polysilicon mass while maintaining heat to said mass sufficient to keep same in a molten condition;
- (d) reducing the amount of infrared heat passing through into the interior of said crucible at that portion of said crucible above said molten polysilicon mass during said drawing of said silicon single crystal by
- (e) placing a thermal shield between said infrared radiation and said crucible at that portion of said crucible which is above the level of said molten polysilicon, said thermal shield comprising fused quartz containing a disperse phase of from about 25 ppm up to about 2000 ppm by weight of fine size, spherically-shaped silicon metal crystals uniformly distributed throughout so as to reduce infrared optical transmission through said shield to a room temperature value no greater than about 30% at a 3 mm sample thickness.
Dependencies are inferred from the claim text.