Method for the production of refractory bricks
AssigneeDyko Industriekeramik GmbH
InventorKlaus Wachter
Life of this patent
Estimating the term…
Abstract
A method for the production of refractory bricks, major components of which are a high proportion of chromium oxide and a small proportion of titanium oxide, makes provision for the chromium oxide and titanium oxide to be mixed, moulded and fired in a reducing atmosphere in order to achieve a solid solution of the titanium oxide in the chromium oxide. The fired intermediate units are then crushed. Other units are then formed from the sieve fractions of the crushed intermediate units and these are fired in a second firing operation to produce the refractory bricks. Non-fired chromium oxide is added to the sieve fractions of the crushed intermediate units and mixed in with this. The other units which are to be reductive-fired in the second firing operation are formed from this mixture.
Claims11
A method for producing a porous chromium oxide containing refractory brick having a firing shrinkage less than 1.0% comprising:
- (a) mixing chromium oxide and titanium oxide to form a first mixture having at least approximately 95% chromium oxide and approximately 5.0% titanium oxide;
- (b) molding and reductive firing the first mixture of chromium oxide and titanium oxide to form intermediate units of solid titanium oxide in the chromium oxide;
- (c) crushing the intermediate units to form sieve fractions;
- (d) mixing the sieve fractions with non-fired chromium oxide to form a second mixture;
- and
- (e) reductive firing the second mixture to form a porous refractory brick having a firing shrinkage less than 1.0% and containing chromium oxide.
A method for producing a refractory brick having a 10 to 20% open pore ratio and a firing shrinkage less than 1.0%, comprising;
- (a) mixing chromium oxide and titanium oxide to form a first mixture having at least 95% chromium oxide and up to approximately 5.0% titanium oxide;
- (b) molding and reductive firing the first mixture to form intermediate units of solid titanium oxide in the chromium oxide;
- (c) crushing the intermediate units to form sieve fractions;
- (d) mixing the sieve fractions with non-fired chromium oxide to form a second mixture;
- and
- (e) reductive firing the second mixture to form a refractory brick having a 18 to 20% open pore ratio and a firing shrinkage less than 1%.
Dependencies are inferred from the claim text.