Method of preparing fluoroplogopite phosphor
AssigneeGTE Products Corporation
InventorsVaddi B. Reddy, Ronald E. Karam, Shellie K. Northrop
Life of this patent
Estimating the term…
Abstract
Electroluminescent phosphors having substantially increased luminance and maintenance over that of prior art electroluminescent phosphors may be made by (1) doping an inorganic intercalation compound having an atomic structure interspersed with vacant spaces, with selected activator ions capable of luminescent emission, and (2) introducing organic monomers or other conductive material into the vacant spaces of the atomic structure of the doped inorganic intercalation compound. The organic monomers may be polymerized in situ to form conductive polymers therein.
Claims9
A method of making a green-emitting titanium-activated fluorophlogopite phosphor having a platelet particle morphology and having the general formula KMg.sub.3 (Si.sub.3 Al)O.sub.10 F.sub.2 :Ti, comprising the steps of:
- combining potassium carbonate, aluminum oxide, magnesium oxide, silicon dioxide, potassium hexafluorosilicate, and titanium dioxide in amounts corresponding to said general formula, to form a uniform mixture, firing said mixture in air at about 1200.degree. C. for about 12 hours to obtain a fired cake, and pulverizing and screening said fired cake to obtain a green-emitting titanium-activated fluorophlogopite phosphor.
A method of making a red-emitting manganese-activated fluorophlogopite phosphor having a platelet particle morphology and having the general formula KMg.sub.3 (Si.sub.3 Al)O.sub.10 F.sub.2 :Mn, comprising the steps of:
- combining potassium carbonate, aluminum oxide, magnesium oxide, silicon dioxide, potassium hexafluorosilicate, and manganese carbonate in amounts corresponding to said general formula to form a uniform mixture, firing said mixture in a covered container in the presence of graphite at about 1200.degree. C. for about 12 hours to obtain a fired cake, and pulverizing and screening said fired cake to obtain a red-emitting manganese-activated fluorophlogopite phosphor.
A method of making a green-emitting terbium-activated fluorophlogopite phosphor having a platelet particle morphology and having the general formula KMg.sub.3 (Si.sub.3 Al)O.sub.10 F.sub.2 :Tb, comprising the steps of:
- combining potassium carbonate, aluminum oxide, magnesium oxide, silicon dioxide, potassium hexafluorosilicate, and terbium fluoride in amounts corresponding to said general formula, to form a uniform mixture, firing said mixture in a covered container in the presence of graphite at about 1200.degree. C. for about 12 hours to obtain a fired cake, and pulverizing, screening and washing said fired cake to obtain a green-emitting terbium-activated fluorophlogopite phosphor.
Dependencies are inferred from the claim text.