Adhesive resin composition

An adhesive resin composition consisting essentially of

• a mixture of at least one crystalline polyolefin resin (A) selected from the group consisting of low density polyethylene, high density polyethylene and copolymers of ethylene and an .alpha.-olefin of at least 3 carbon atoms and have an ethylene content of 90% by weight or more, and 45-95% by weight of an amorphous or low crystalline olefin copolymer of ethylene and an .alpha.-olefin having at least 3 carbon atoms (B),
• maleic anhydride, and
• at least one crystalline polyolefin resin (E) selected from the group consisting of low density polyethylene, high density polyethylene, linear low density polyethylene, copolymers of ethylene and any one of vinyl acetate, acrylic acid and their esters and obtained by
• (a) mixing
• (i) 0.01-5 parts by weight of maleic anhydride,
• (ii) 0.01-2 parts by weight of a free-radical initiator (D), and
• (iii) 100 parts by weight of a mixture consisting of 55-5% by weight of a crystalline polyolefin resin (A) selected from the group consisting of low density polyethylene, high density polyethylene, and copolymers of ethylene and an .alpha.-olefin of at least 3 carbon atoms which copolymers have an ethylene content of 90% by weight or more and 45-95% by weight of an amorphous or low crystalline olefin copolymer of ethylene and an .alpha.-olefin having at least 3 carbon atoms (B),
• to obtain a precursor mixture,
• (b) melt-kneading the precursor mixture in the first half stage of a twin-screw extruder having at least one side feeder provided at at least one portion of said extruder, the location of said one side feeder being selected from the group consisting of the midway stage of the extruder and the latter half stage of the extruder, to obtain a modified precursor mixture, and
• (c) feeding a crystalline polyolefin resin (E) selected from the group consisting of low density polyethylene, high density polyethylene, linear low density polyethylene, and copolymers of ethylene and any one of vinyl acetate, acrylic acid and their esters from the at least one side feeder of the extruder and mixing the resin (E) with the modified precursor mixture so that the ratio of the total weight of the components (A) and (B) to the weight of the component (E) is within the range of from 60:40 to 2:98.