Method treating terne steel
AssigneeThe Louis Berkman Company
InventorsJay F. Carey, II, Mehrooz Zamanzadeh
Life of this patent
Estimating the term…
Abstract
A method of treating a terne coating to accelerate the patina on the terne coating. The terne coated metal is coated with a specially formulated asphalt based paint which produces a semi-transparent or translucent, dull finish on the terne coated metal. The coated terne coated metal is then exposed to the natural atmospheric elements for at least six months wherein such time enhanced oxidation of lead and tin occurs.
Claims13
A coated steel sheet member that exhibits high resistance to corrosion and having accelerated terne patina formation when exposed to the atmosphere to produce a dull, iron oxide corrosion resisting finish, said sheet member including an outer layer of an alloy of lead and tin to produce a terne coated metal coated with a translucent layer of an asphalt base paint having a thickness of not more than 1.0 mil which accelerates said patina formation, said asphalt base paint comprises the following weight percentages:
- asphalt 60-80%, titanium oxide (anatase and rutile) 1.0-25.0%, inert silicates or clay 8.0-11.0%, carbon black 0.5-2.0% and antisettling agent 0.4-0.7%.
A terne coated steel strip having a thin translucent film of less than 1.0 mil in thickness and permeable to both moisture and ultraviolet rays and containing a suspension of free carbon particles and a system causing said film to deteriorate after four to six months of exposure to sunlight, said suspension comprising:
- asphalt 60-80%, titanium oxide (anatase and rutile) 1.0-25.0%, inert silicates or clay 8.0-11.0%, carbon black 0.5-2.0% and antisettling agent 0.4-0.7%.
A terne coated metal having accelerated patina formation of the tin and lead alloy, said metal being coated with a translucent layer of paint of a thickness of not more than 1.0 mil which accelerates said patina formatoin and comprises 0.7% carbon black, 18.65% titanium oxide, 9.32% calcium borosilicate, 70.86% gilsonite and 0.47% antisettling agent.