Rhombohedral calcium carbonate and accelerated heat-aging process for the production thereof

A process for producing a calcium carbonate product having a blocky rhombohedral or a hexagonal prismatic calcite crystal structure and properties including a surface area of from about 3 to about 15 m.sup.2 /g, an average particle size of from about 0.2 to about 0.9 micron, a discrete particle aspect ratio of less than about 2:1 , and a particle size distribution such that at least about 60 weight percent of the discrete particles have a size within 50 percent of the equivalent discrete particle average spherical diameter, said process consisting essentially of:

• a) forming an aqueous slurry of a calcium carbonate having a crystal structure selected from the group consisting of blocky rhombohedral, scalenohedral, hexagonal prismatic and substantially spherical calcite, and needle-like aragonite with an aspect ratio greater than about 2:1;
• said selected calcium carbonate having properties including a surface area greater than about 15 m.sup.2 /g and an average discrete particle size of from about 0.01 to about 0.8 micron;
• b) placing the slurry in a hydrothermal bomb;
• c) sealing said bomb;
• d) raising the temperature in the bomb to a hydrothermal aging temperature of the slurry of up to about 300.degree. C., to initiate hydrothermal heat aging;
• e) maintaining the slurry in the hydrothermal bomb at the hydrothermal aging temperature and at the resultant bomb pressure, for a time in the range of from about 1 to about 24 hours, said time being sufficient to cause the crystal structure and properties of the calcium carbonate feedstock to rearrange to the product form, said time within the range being determined by the nature of the calcium carbonate feedstock, and said time being such that it is less than the time required for a given calcium carbonate feestock to rearrange to the product form by Ostwald ripening;
• and
• f) terminating hydrothermal heat aging by rapidly lowering the bomb pressure and temperature to fix the crystal structure and properties of the calcium carbonate in the product form.