Alkaline resol phenol-aldehyde resin binder composition
AssigneeFoseco International Limited
InventorsGarry Smith, Martin Bradley
Life of this patent
Estimating the term…
Abstract
A binder composition for producing articles of bonded particulate material such as foundry molds or core comprises an alkaline aqueous solution of a resol phenol-aldehyde resin, an oxyanion which can form a stable complex with the resin, and an ethylene glycol monoalkyl ether. The binder composition has an alkali to phenol molar ratio of from 1.5:1 to 2.5:1 and the amount of alkali present in the solution is sufficient to substantially prevent stable complex formation between the resin ad the oxyanion. Bonded articles are produced by passing carbon dioxide gas through articles formed from a mixture of particulate material and the binder composition so as to produce stable complex formation and curing of the resin.
Claims14
A binder composition for forming foundry molds or cores comprising an alkaline aqueous solution of a resol phenol-aldehyde resin and an oxyanion which can form a stable complex with the resin, the amount of alkali present in the solution being sufficient to solubilize the resin and to substantially prevent stable complex formation between the resin and the oxyanion wherein the molar ratio of alkali to phenol is from 1.5:1 to 2.5:1 and the binder composition also contains an ethylene glycol monoalkyl ether in an amount sufficient to improve foundry mold or core strength immediately after gassing with carbon dioxide and after storage.
A process for the production of a mold or core of bonded particulate material, comprising the steps of:
- (i) forming a mixture of a binder and particulate material to a desired shape, the binder comprising:
- an alkaline aqueous solution of a resol phenolaldehyde resin having an alkali to phenol molar ratio of from 1.5:1 to 2.5:1;
- an oxyanion which can form a stable complex with the resin;
- and an ethylene glycol monoalkyl ether;
- the amount of alkali present in the solution being sufficient to solubilise the resin and to substantially prevent stable complex formation between the resin and the oxyanion and the amount of ethylene glycol monoalkyl ether being sufficient to improve foundry mold or core strength immediately after gassing with carbon dioxide and after storage
- (ii) passing carbon dioxide gas through the formed shape so as to cause the oxyanion to form a stable complex with the resin;
- and
- (iii) curing the resin to form a mold or core of bonded particulate material.
A binder composition for forming foundry molds and cores, comprising:
- an oxyanion;
- an alkaline aqueous solution of a resol phenol-aldehyde resin in a molar ratio of alkali to phenol in the range of 1.5:1 to 2.5:1 and the alkali being present in an amount to solubilise the resin and to substantially prevent the formation of stable complexes between the resin and the oxyanion;
- an ethylene glycol monoalkyl ether in an amount sufficient to improve foundry mold or core strength immediately after gassing with carbon dioxide and after storage;
- and wherein the binder composition produces foundry molds and cores having improved strength, surface finish and edge hardness.
Dependencies are inferred from the claim text.