Method of producing low temperature firing dielectric ceramic composition containing B.sub.2 O.sub.3

Abstract

A method of producing a dielectric ceramic composition is disclosed which includes the steps of: preparing a main ceramic composition comprising BaO, TiO, and RE.sub.2 O.sub.3 (where RE represents at least one rare earth metal) as major components; calcining a mixture of starting materials which give the main ceramic composition, at a temperature of 1050.degree. C. or higher, to provide a calcined mixture; finely pulverizing the calcined mixture to provide a calcined ceramic powder having an average grain size of not larger than 0.8 .mu.m; and adding, as at least a part of a secondary component, a B.sub.2 O.sub.3 powder or a glass powder containing B.sub.2 O.sub.3, to the main ceramic composition. Also disclosed are a dielectric resonator and dielectric filter using such a dielectric ceramic composition as produced according to the above method, and a method of producing such a dielectric resonator or filter.

Dependencies are inferred from the claim text.