Process for preparing silver-palladium powders

A process for preparation of silver-palladium fine powders comprising the steps of:

• (a) dissolving palladium nitrate and silver in aqueous nitric acid solutions separately, mixing the resulting aqueous nitric acid solutions and diluting the mixed nitric acid solution with pure water until a pH value of 0.5-2.0 is obtained;
• (b) preparing an aqueous solution of a hydrazine and a surfactant system containing 0.5-5.0% of caprylic acid and 0.5-5.0% of triethanolamine, based on the volume of the aqueous solution, or 0.25-1.30% of oleic acid and 0.25-1.30% of triethanolamine, based on the volume of the aqueous solution;
• (c) adding the diluted mixed nitric acid solution from step (a) to the aqueous solution from step (b) while stirring at 200-500 rpm to effectuate a reduction reaction such that the silver and palladium ions contained in the diluted mixed nitric acid solution are reduced to their corresponding metals, respectively, and precipitated therefrom, wherein the amount of hydrazine contained in the aqueous solution is 1-10 times the stoichiometric amount needed to reduce the silver and palladium ions, and the reduction reaction is carried out at 35.degree.-50.degree. C., and
• (d) recovering said precipitated silver and palladium metals from said reaction mixture by filtration, washing the recovered silver and palladium metals with an organic solvent and water, and drying the washed metals to obtain silver-palladium fine powders.