Abstract
The present invention relates to a process for continuously recycling water soluble resin whereby a resin solution including about 6-12 percent by weight of resin is sprayed onto a core made of the resin. The resin used for the solution and core is selected from polyacrylic acid, copolymers of acrylic acid and acrylamide, copolymers of acrylic acid salt and ethyl acrylate, copolymers of acrylamide and acrylic acid, polymethacrylic acid, and copolymers of vinyl alcohol and vinyl acetate. The spraying of the resin solution dissolves the core to form a polymer suspension from which resin is recovered for reuse.
Claims9
A process for continuously recycling water soluble resin, comprising the steps of:
- preparing a resin solution comprising about 6-12 percent by weight of polyacrylic acid;
- heating the resin solution to a temperature of about 88.degree. C. to 99.degree. C.;
- spraying the heated resin solution at a pressure of about 2.8 to 4.9 kg/cm.sup.2 onto a core made of resin comprising polyacrylic acid to dissolve said core to form a polymer suspension;
- directing a first portion of the polymer suspension to a separator to remove water therefrom to from a resin product concentrate;
- and
- recirculating a second portion of the polymer suspension for reuse in preparing the resin solution.
A process for continuously recycling water soluble resin, comprising the steps of:
- preparing a resin solution comprising about 6-12 percent by weight of copolymers of acrylic acid and acrylamide;
- heating the resin solution to a temperature of about 88.degree. C. to 99.degree. C.;
- spraying the heated resin solution at a pressure of about 2.8 to 4.9 kg/cm.sup.2 onto a core made of resin comprising copolymers of acrylic acid and acrylamide to dissolve said core to form a polymer suspension;
- directing a first portion of the polymer suspension to a separator to remove water therefrom to from a resin product concentrate;
- and
- recirculating a second portion of the polymer suspension for reuse in preparing the resin solution.
A process for continuously recycling water soluble resin, comprising the steps of:
- preparing a resin solution comprising about 6-12 percent by weight of copolymers of acrylic acid and ethyl acrylate;
- heating the resin solution to a temperature of about 88.degree. C. to 99.degree. C.;
- spraying the heated resin solution at a pressure of about 2.8 to 4.9 kg/cm.sup.2 onto a core made of resin comprising copolymers of acrylic acid and ethyl acrylate to dissolve said core to form a polymer suspension;
- directing a first portion of the polymer suspension to a separator to remove water therefrom to from a resin product concentrate;
- and
- recirculating a second portion of the polymer suspension for reuse in preparing the resin solution.
A process for continuously recycling water soluble resin, comprising the steps of:
- preparing a resin solution comprising about 6-12 percent by weight of one or more polymers selected from the group consisting of copolymers of acrylic acid salt and ethyl acrylate, polymethyacrylic acid, and copolymers of vinyl alcohol and vinyl acetate;
- heating the resin solution to a temperature of about 88.degree. C. to 99.degree. C.;
- spraying the heated resin solution at a pressure of about 2.8 to 4.9 kg/cm.sup.2 onto a core to dissolve said core to form a polymer suspension wherein the core is made of the same polymers that form the resin solution;
- directing a first portion of the polymer suspension to a separator to remove water therefrom to from a resin product concentrate;
- and
- recirculating a second portion of the polymer suspension for reuse in preparing the resin solution.