Silver paste sintering method for bonding ceramic surfaces

A solid state silver sintering method for bonding a first preformed ceramic element having a first faying surface to a second preformed ceramic element having a second faying surface, said method using a silver powder paste composed of silver particles dispersed in a volatile solvent vehicle comprising a vaporizable organic binder, said method comprising

• applying and drying said paste onto said first faying surface to form a first film composed predominantly of said silver particles and having a thickness greater than about 20 microns,
• applying and drying said paste onto said second faying surface to form a second film composed predominantly of said silver particles and having a thickness greater than about 20 microns,
• assembling said first element and said second element with said first powder film in contact with said second powder film, and
• heating the assembly at a temperature and for a time sufficient to sinter the silver particles into an integral silver layer having a thickness greater than about 30 microns and to bond said silver layer to the adjacent ceramic surfaces to thereby bond the elements into a product assembly, wherein said temperature is less than the melting point of silver.

A method of manufacturing a stripline filter comprising a first ceramic element having a first preformed faying surface, a second ceramic element having a second preformed faying surface, and a metallic resonator element interposed between said first faying surface and said second faying surface, said method comprising

• applying and drying said paste onto a region of said first faying surface to form a first film, said paste comprising silver particles dispersed in a volatile solvent vehicle, said first film being applied in a pattern corresponding to a desired resonator configuration,
• applying and drying a second film of said paste onto said second faying surface, said second film being applied in a configuration superposable onto the first film,
• assembling said first element and said second element with said first film superposed in contact with said second film, and
• heating the assembly to a temperature and for a time sufficient to sinter said particles into an integral silver layer and to bond said silver layer to an adjacent ceramic surface to form the filter, wherein said temperature is less than the melting point of silver.

A method of manufacturing a stripline filter comprising a first ceramic element having a first preformed faying surface, a second ceramic element having a second preformed faying surface, and a metallic resonator element interposed between said first faying surface and said second faying surface, said method comprising

• applying and drying a paste onto a region of said first faying surface to form a first film, said paste comprising silver particles dispersed in a volatile solvent vehicle and containing a vaporizable organic compound suitable for bonding the silver particles into the film, said first film being composed predominantly of said silver particles and having a thickness of at least 20 microns, said first film being applied in a pattern corresponding to a desired resonator configuration,
• applying and drying said paste onto said second faying surface to form a second film, said second film being composed predominantly of said silver particles and having a thickness of at least 20 microns, said second film being applied in a configuration superposable onto the first film,
• assembling said first element and said second element with said second film superposed in contact with said first film, and
• heating the assembly to a temperature between about 850.degree. C. and 930.degree. C. for a time sufficient to vaporize the organic compound and to sinter said particles into an integral silver layer having a thickness of at least about 30 microns and to bond said silver layer to an adjacent ceramic surface to form the filter, whereby said silver layer forms a resonator of said filter.