Dental porcelain for titanium and titanium alloys
AssigneeAmerican Thermocraft Corporation Subsidiary of Jeneric/Pentron Incorporated
InventorsCarlino Panzera, Arun Prasad
Life of this patent
Estimating the term…
Abstract
Porcelain compositions suitable for use as porcelain layers on metal base dental restorations have fusion temperatures of about 800.degree. C. and lower. The compositions may be employed as coatings on titanium and titanium alloy bases since the compositions have thermal expansion values close to those of titanium and its alloys. A method is also provided for forming dental restorations with relatively inexpensive and biocompatible metal bases and low fusing dental porcelains.
Claims16
A dental restoration comprising a titanium or titanium alloy coping coated with a biocompatible porcelain composition, said porcelain composition consisting essentially of:
- Component (A) 50-70 percent by weight silicon dioxide,
- Component (B) 7-33 percent by weight boron oxide,
- Component (C) at least 8 percent by weight zinc oxide,
- Component (D) up to 4 percent by weight aluminum oxide,
- Component (E) up to 4 percent by weight titanium dioxide,
- Component (F) up to 12 percent by weight sodium oxide,
- Component (G) up to 8 percent by weight potassium oxide,
- Component (H) up to 3 percent by weight cerium oxide,
- Component (I) up to 1 percent by weight zirconium oxide, and
- Component (J) up to 1 percent by weight of a complex of yttrium oxide and cerium oxide,
- said composition having a thermal expansion coefficient close to that of said titanium or titanium alloy coping, having a fusion temperature of about 800.degree. C. or lower, and capable of being shaped in the form of a finished crown or multiple unit bridge.
A dental restoration comprising a titanium or titanium alloy coping coated with a biocompatible porcelain composition, said porcelain composition consisting essentially of a mixture of a first component mixture and a second component mixture, said first component mixture comprising 70-80 percent by weight of said porcelain composition and consisting essentially of:
- Component (A) 50-70 percent by weight silicon dioxide,
- Component (B) 7-33 percent by weight boron oxide,
- Component (C) at least 8 percent by weight zinc oxide,
- Component (D) up to 4 percent by weight aluminum oxide,
- Component (E) up to 4 percent by weight titanium dioxide,
- Component (F) up to 12 percent by weight sodium oxide,
- Component (G) up to 8 percent by weight potassium oxide,
- Component (H) up to 3 percent by weight cerium oxide,
- Component (I) up to 1 percent by weight zirconium oxide, and
- Component (J) up to 1 percent by weight of a complex of yttrium oxide and cerium oxide, said first component mixture being capable of being shaped in the form of a finished crown or multiple unit bridge,
- said second component mixture comprising 20-30 percent by weight of said porcelain composition and consisting essentially of:
- Component (K) up to 100 percent by weight titanium dioxide,
- Component (L) up to 100 percent by weight cerium oxide,
- Component (M) up to 100 percent by weight stannous oxide, and
- Component (N) up to 100 percent by weight zinc oxide, said porcelain composition having a thermal expansion coefficient close to that of titanium and a fusion temperature of about 800.degree. C. or lower.
A dental restoraton comprising a titanium or titanium alloy coping coated with a biocompatible opaque porcelain composition and wherein said opaque porcelain is coated with a biocompatible body porcelain composition, wherein said body porcelain composition consists essentially of:
- Component (A) 50-70 percent by weight silicon dioxide,
- Component (B) 7-33 percent by weight boron oxide,
- Component (C) at least 8 percent by weight zinc oxide,
- Component (D) up to 4 percent by weight aluminum oxide,
- Component (E) up to 4 percent by weight titanium dioxide,
- Component (F) up to 12 percent by weight sodium oxide,
- Component (G) up to 8 percent by weight potassium oxide,
- Component (H) up to 3 percent by weight cerium oxide,
- Component (I) up to 1 percent by weight zirconum oxide, and
- Component (J) up to 1 percent by weight of a complex of yttrium oxide and cerium oxide,
- said body porcelain composition having a thermal expansion coefficient close to that of said titanium or titanium alloy coping, having a fusion temperature of about 800.degree. C. or lower, and being capable of being shaped in the form of a finished crown or multiple unit bridge, and
- wherein said opaque porcelain composition consists essentially of a mixture of a first component mixture and a second component mixture, said first component mixture comprising 70-80 percent by weight of said opaque porcelain composition and consisting essentially of:
- Component (A1) 50-70 percent by weight silicon dioxide,
- Component (B1) 7-33 percent by weight boron oxide,
- Component (C1) at least 8 percent by weight zinc oxide,
- Component (D1) up to 4 percent by weight aluminum oxide,
- Component (E1) up to 4 percent by weight titanium dioxide,
- Component (F1) up to 12 percent by weight sodium oxide,
- Component (G1) up to 8 percent by weight potassium oxide,
- Component (H1) up to 3 percent by weight caerium oxide,
- Component (I1) up to 1 percent by weight zirconium oxide, and
- Component (J1) up to 1 percent by weight of a complex of yttrium oxide and cerium oxide,
- said second component mixture comprising 20-30 percent by weight of said opaque porcelain composition and consisting essentially of:
- Component (K) up to 100 percent by weight titanium dioxide,
- Component (L) up to 100 percent by weight cerium oxide,
- Component (M) up to 100 percent by weight stannous oxide, and
- Component (N) up to 100 percent by weight zinc oxide,
- said opaque porcelain composition having a thermal expansion coefficient close to that of said titanium or titanium alloy coping and a fusion temperature of about 800.degree. C. or lower.
Dependencies are inferred from the claim text.