US 5,281,271 AGranted
Cement based paint and finishing composition
AssigneeHITEK Fine Chemicals Pvt. Ltd.
InventorsKishore K. Govani, Bhanu K. Govani, Ramesh K. Govani
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeHITEK Fine Chemicals Pvt. Ltd.
InventorsKishore K. Govani, Bhanu K. Govani, Ramesh K. Govani
Estimating the term…
Cement based finishing compositions are disclosed in which use of portland cement as a binder is significantly reduced without adversely affecting bonding or adhesion and while enhancing coverage of surface area, workability and hiding power or opaqueness. The composition, when mixed with an appropriate amount of water can be applied in a single coating over a primed surface on a masonry, concrete, sand rendering, brick work, cement blocks and the like to give a finished, homogenous surface. In another embodiment a floor and wall topper composition is disclosed which, when mixed with water at lower than conventional proportions, provides a rock-hard, either jointless or compartmented sections having improved compressive and flexural strength and resistance to wear and tear.
A composition for forming cement finishing materials comprising, by weight, 12-25% portland cement, 25-35% calcium hydroxide, 12-16% magnesium oxide, 25-32% silicon dioxide, 1-3% zinc oxide, 0.5-3% aluminum stearate, 0.05-3% melamine formaldehyde, and 0.5-10% coloring agents.
A composition for forming cement finishing materials comprising by weight, 12-25% portland cement, 25-35% calcium hydroxide, 0.05-3% melamine formaldehyde as binders and 12-16% magensium oxide and 25-32% silicon dioxide as fillers, all having a particle size no larger than approximately 69 microns.
A composition for forming cement finishing materials comprising, by volume, 55-70% white portland cement, 13-25% calcium hydroxide, 2-5% magnesium oxide, 3-8% silicon dioxide, 1-4% aluminum oxide, 1-3% aluminum stearate, 0.005-1% melamine formaldehyde, 1-10% oxide pigments for inorganic coloring and 0.01-0.5% surfactants.
A composition for forming cement finishing materials comprising, by volume, 55-70% portland cement, 13-25% calcium hydroxide and 0.005-1% melamine formaldehyde as binders, 2-5% magnesium oxide, 3-10% silicon dioxide, 1-4% aluminum oxide, and 1-3% aluminum stearate as fillers, and 0.01-0.5% surfactants.
Dependencies are inferred from the claim text.