Composite fiberboard and process of manufacture
AssigneeArmstrong World Industries, Inc.
InventorsJohn Felegi, Jr., Kenneth P. Kehrer, Edward E. Wise, Jr.
Life of this patent
Estimating the term…
Abstract
A novel composite board of mineral wool, perlite, and cellulosic newsprint fibers for use as an acoustical tile is disclosed. The board displays a high porosity, a fine pore structure, a low density gradient through its thickness and an acceptable strength. The board is manufactured by a process that includes a flotation step prior to the final formation step.
Claims9
A process for manufacturing a composite board product having a thickness of at least 0.5 inch and consisting essentially of up to 87% mineral wool, 5-75% perlite, 4-35% by weight cellulose fibers, 0-25% clay, and 2-15% by weight of a latex binder composition which comprises mixing the components with water to form an aqueous slurry;
- feeding said slurry into an initial zone;
- retaining said formed slurry in said zone without any further treatment for a time sufficient for turbulence to cease and for said cellulose fibers to disperse substantially uniformly throughout the thickness of said slurry;
- and, immediately thereafter, transferring said slurry to the final forming zone wherein the formed material is drained of liquid and pressed into the shape of said product having a thickness of at least 0.5 inch;
- and heating to solidify said product.
A composite board having a thickness of at least 0.5 inch consisting essentially of up to 87% by weight mineral wool, 5-85% by weight perlite, 0-25% by weight clay, 4-35% by weight cellulosic fibers, and 2-15% by weight of a binder composition comprising at least one thermoplastic polymer having a glass transition temperature of from 80.degree. C. to 115.degree. C., wherein the cellulose fibers in said board are substantially completely coated with said binder composition, said board displaying a density profile difference from front to back of less than about 0.05 pound per board foot and a noise resistance coefficient of at least 0.60.
A process for manufacturing a composite board product having a thickness of at least 0.5 inch and consisting essentially of up to 87% mineral wool, 5-75% perlite, 4-35% by weight cellulose fibers, 0-25% clay, and 2-15% by weight of a binder composition which comprises mixing the components with water to form an aqueous slurry;
- feeding said slurry into an initial zone;
- retaining said formed slurry in said zone without any further treatment for a time sufficient for any turbulence to cease and for said cellulose fibers to disperse substantially uniformly throughout the thickness of said slurry;
- and, immediately thereafter, transferring said slurry to the final forming zone wherein the formed material is drained of liquid and pressed into the shape of said product having a thickness of at least 0.5 inch;
- and heating to solidify said product.
A composite board having a thickness of at least 0.5 inch consisting essentially of up to 87% by weight mineral wool, 5-85% by weight perlite, 0-25% by weight clay, 4-35% by weight of cellulosic fibers, and 2-15% by weight of a binder composition, said board displaying a density profile difference from front to back of less than about 0.05 pound per board foot and a noise resistance coefficient of at least 0.60.
Dependencies are inferred from the claim text.