Method of forming a cross linked foamed polyolefin article
AssigneeOhio Cellular Products, Inc.
InventorsDonald E. Nelson, James E. Lammy, Sr.
Life of this patent
Estimating the term…
Abstract
A method for forming soft, resilient, smooth, energy dissipating articles from foamed partially cross-linked polyolefins wherein sheet stock is cut into a preform and the preform while at room temperature is positioned within a mold cavity formed by partible mold halves. The preforms and the cavity of the molds are so arranged and constructed that after molding there is no flashing needing trimming because the polyolefin is substantially confined within the cavity without any lateral projection into the parting surfaces of the mold.
Claims23
A method for forming a foamed, cross-linked polyolefin into an article in a mold having partible mold portions, said mold, when in a closed position, defining an article forming cavity which includes a smooth arcuate edge and said mold having a peripheral parting surface, said method comprising the steps of:
- cutting sheet stock of foamed, cross-linked polyolefin into a preform having a rough edge, said polyolefin being at least capable of being sufficiently thermoformed to allow a rough edge to be formed into a smooth edge, and said preform, in plan view, having a peripheral configuration substantially corresponding to the peripheral shape of the cavity in plan peripheral view;
- positioning said preform, below the temperature at which said preform is rendered tacky or sticky, into a mold portion so that, upon closing and heating the mold, said preform is placed in compressive contact with the cavity and is substantially confined within said cavity without laterally projecting into said peripheral parting surface;
- and heating a closed mold containing said preform for a sufficient period of time to allow said rough edge of said polyolefin to be formed into a smooth edge by contact with said smooth edge of said mold cavity.
A method for forming a foamed, cross-linked polyolefin into an article in a mold having partible mold portions, said mold, when in a closed position, defining an article forming cavity and having a peripheral parting surface, the method comprising the steps of:
- cutting stock of said polyolefin into a preform;
- positioning said preform, below the temperature at which said preform is rendered tacky or sticky, into said mold so that, upon closing said mold and heating same, said mold cavity is filled with said preform but said preform does not laterally extend into said peripheral parting surface;
- and closing said mold and heating said closed mold containing said preform for a sufficient period of time for said preform to conform to the adjacent mold cavity.
A method for molding a foamed cross-linked polyolefin in a mold having partible mold portions comprising the steps of:
- positioning said foamed cross-linked polyolefin, below the temperature at which said polyolefin is rendered tacky or sticky, in a cavity portion of said mold;
- closing said partible mold portions;
- and heating said mold and said polyolefin so as to mold and conform outer portions of said polyolefin to the surface of the mold cavity;
- the amount of polyolefin being such that, during said heating step, substantially no polyolefin extends into the mating parting surfaces of the closed partible mold portions.
A method for forming a molded, foamed, cross-linked polyolefin article which is substantially free of flashing in a mold having partible mold halves which, when closed, define a cavity and a contiguous peripheral mold parting line, said method comprising the steps of:
- positioning formed cross-linked polyolefin, below the temperature at which said polyolefin is rendered tacky or sticky, into a cavity portion of said mold;
- closing said mold;
- and heating said mold for a sufficient period of time to form said article.
Dependencies are inferred from the claim text.