Method of manufacturing an heteroepitaxial semiconductor structure
AssigneeGTE Laboratories Incorporated
InventorsBen G. Yacobi, Stanley Zemon, Chirravuri Jagannath
Life of this patent
Estimating the term…
Abstract
Heteroepitaxial semiconductor structures of, for example, GaAs on InP or Si. The epitaxially grown GaAs is in the form of individual spaced-apart islands having maximum dimensions in the plane of the surface of the substrate of no greater than 10 micrometers. In islands of this size stress in the plane of the epitaxially grown layers due to mismatch of the coefficients of thermal expansion of the substrate and epitaxially grown materials is insignificant.
Claims12
The method of fabricating a semiconductor structure comprising:
- providing a substrate of essentially single crystal insulating or semiconducting material having a flat, planar surface;
- forming on said surface of the substrate an epitaxial layer consisting of a plurality of individual islands of single crystal semiconductor material having a different coefficient of thermal expansion from that of the substrate material, said islands being spaced from each other;
- wherein:
- forming on said surface of the substrate an epitaxial layer includes growing a layer having a flat, planar upper surface substantially parallel to said surface of the substrate;
- each of said islands has edge surfaces extending from the upper surface to the surface of the substrate;
- and
- the maximum distance between edge surfaces of each island is no greater than about 10 micrometers.
The method of fabricating a semiconductor structure comprising:
- providing a substrate of essentially single crystal insulating or semiconducting material having a flat, planar surface;
- epitaxially growing on said surface of the substrate an epitaxial layer of single crystal semiconductor material having a different coefficient of thermal expansion from that of the substrate material, said epitaxial layer having a flat, planar upper surface substantially parallel to said surface of the substrate;
- removing semiconductor material of said epitaxial layer to leave a plurality of individual islands of single crystal semiconductor material spaced from each other;
- each of said islands having edge surfaces extending from said upper surface to the surface of the substrate;
- and
- the maximum distance between edge surfaces of each island being no greater than about 10 micrometers.
The method of fabricating a semiconductor structure comprising:
- providing a substrate of essentially single crystal insulating or semiconducting material having a flat, planar surface;
- covering said surface of the substrate with a coating of an adherent protective material;
- selectively removing portions of said coating to expose a plurality of individual areas of said surface of the substrate each encircled by material of said coating;
- epitaxially growing an epitaxial layer consisting of a plurality of individual islands of single crystal semiconductor material having a different coefficient of thermal expansion from that of the substrate material, each island being epitaxially grown on one of the individual exposed areas of said surface of the substrate and said epitaxial layer having a flat, planar upper surface substantially parallel to said surface of the substrate;
- each of said islands having edge surfaces extending from the upper surface to the surface of the substrate;
- and
- the maximum distance between edge surfaces of each island being no greater than about 10 microns;
- and
- removing the remainder of said coating to leave a plurality of individual islands of single crystal semiconductor material spaced from each other.
Dependencies are inferred from the claim text.