Supported microporous ceramic membranes
AssigneeWisconsin Alumni Research Foundation
InventorsElizabeth Webster, Marc Anderson
Life of this patent
Estimating the term…
Abstract
A method for permformation of microporous ceramic membranes onto a porous support includes placing a colloidal suspension of metal or metal oxide particles on one side of the porous support and exposing the other side of the porous support to a drying stream of gas or a reactive gas stream so that the particles are deposited on the drying side of the support as a gel. The gel so deposited can be sintered to form a supported ceramic membrane useful for ultrafiltration, reverse osmosis, or molecular sieving having mean pore sizes less than 100 Angstroms.
Claims29
A method of preparing a microporous metal oxide ceramic membrane on a porous support with two sides comprising the steps of
- (a) making a colloidal non-polymeric suspension of metal or metal oxide colloidal particles in a solvent;
- (b) exposing the colloidal suspension to one side of the porous support under conditions so that the suspension is drawn by capillary action into the porous support;
- (c) exposing the other side of the support to a gas stream gas under conditions favoring evaporation of the solvent in the colloidal suspension so that a gel layer of metal oxide is deposited on said other side of the porous support;
- (d) drying any remaining solvent from the gel layer;
- and
- (e) firing the support with the gel layer thereon at a temperature sufficient to sinter the gel into a ceramic membrane while maintaining the pores therein.
A method of preparing a microporous metal oxide ceramic membrane on a porous support with two sides comprising the steps of
- (a) making a colloidal suspension of metal or metal oxide colloidal particles in a solvent;
- (b) exposing the colloidal suspension to one side of the porous support under conditions so that the suspension is drawn by capillary action into the porous support;
- (c) exposing the other side of the support to a gas stream gas under conditions favoring evaporation of the solvent in the colloidal suspension so that a gel layer of metal oxide is desposited on said other side of the porous support;
- (d) drying any remaining solvent from the gel layer by exposing the side of the support with the gel thereon to solvent with the other side of the support exposed to drying conditions to draw solvent through the support away from the gel;
- and
- (e) firing the support with the gel layer thereon at a temperature sufficient to sinter the gel into a ceramic membrane while maintaining the pores therein.
A method of permforming a microporous metal oxide ceramic membrane on a porous support comprising the steps of
- (a) making a colloidal non-polymeric suspension of metal or metal oxide particles in a solvent;
- (b) forming a gas stream passage having a drying side and a sol side and including therein the porous support;
- (c) placing the colloidal suspension on the sol side of the gas stream passage;
- (d) causing the flow of gas stream on the drying side of the drying gas passage under conditions so as to cause the evaporation of the solvent through the porous support thereby depositing the metal oxide particles on the drying side of the support as a gel;
- (e) drying the gel thus produced;
- and
- (f) sintering the gel into a microporous ceramic membrane.
A method of performing a microporous metal oxide ceramic membrane on a porous support comprising the steps of
- (a) making a colloidal non-polymeric suspension of metal or metal oxide particles in a solvent;
- (b) forming a gas stream passage having a drying side and a sol side and including therein the porous support;
- (c) placing the colloidal suspension on the sol side of the gas stream passage;
- (d) causing the flow of gas stream on the drying side of the drying gas passage under conditions so as to cause the evaporation of the solvent through the porous support thereby depositing the metal oxide particles on the drying side of the support as a gel;
- (e) drying the gel thus produced by exposing the dry side of the support to solvent and the sol side of the support exposed to drying conditions to draw solvent through the support away from the gel;
- and
- (f) sintering the gel into a microporous ceramic membrane.
Dependencies are inferred from the claim text.