AssigneesKasei Optonix, Ltd., Mitsubishi Kasei Corporation
InventorsHideo Suzuki, Etsuo Shimizu, Yujiro Suzuki, Kitaro Shigeta, Takashi Johnokuchi
Life of this patent
Estimating the term…
Abstract
A calcium tungstate phosphor which comprises calcium tungstate as a host and vanadium, wherein the proportion of the vanadium to the calcium tungstate is within a range of from 0.01 to 30 ppm. The phosphor is produced by forming a solid calcium tungstate precipitate from an aqueous medium containing ammonia, calcium ion, tungstate ion and vanadate ion and firing the precipitate in the presence of fluxing material.
Claims2
A process for producing a calcium tungstate phosphor comprising calcium tungstate as a host and vanadium, said process comprises:
- (a) forming a solid calcium tungstate precipitated from aqueous medium by mixing an aqueous solution containing calcium ion with an aqueous solution containing tungstate ion, ammonia and vanadate ion, in relative amounts required to precipitate solid calcium tungstate wherein the proportion of vanadium to calcium tungstate in said precipitate is within the range of from 0.01-30 ppm,
- (b) separating the precipitated solid calcium tungstate containing vanadium,
- (c) adding a fluxing material selected from the group consisting of CaCl.sub.2, Na.sub.2 CO.sub.3, KNO.sub.3, MgCl.sub.2 and NH.sub.4 Cl to the solid calcium tungstate,
- (d) firing the resultant composition at a temperature of about 600.degree. C. to 1,300.degree. C., and
- (e) washing the first composition with water to remove any residual water-soluble contaminants.
Dependencies are inferred from the claim text.