Gas plasma treatment for archival preservation of manuscripts and the like
AssigneePlasma Plus
InventorsSvetlana A. Krapivina, Georgy Z. Paskalov, Alexander K. Filippov
Life of this patent
Estimating the term…
Abstract
Archival materials including paper manuscripts are preserved by a thin protective polymer film applied to the surface of the item by plasma polymerization of an organic monomer gas in a high frequency glow discharge. The polymer film protects the item against humidity and prevents widening of stroke lines due to ink spreading on the document. Microorganism growth is stopped by pretreatment of the document in a monoatomic gas plasma.
Claims13
A method for preserving archival materials comprising the steps of:
- exposing said materials to a low temperature plasma of organic monomer gas comprised of one or more hydrocarbon gases or a mixture thereof;
- and
- continuing said exposure for a treatment time ranging from 30 to 3600 seconds to form a thin layer of polymer material on the surface of said material.
A method for preserving archival materials, comprising the steps of:
- pretreating said materials in a plasma of a monoatomic gas for a pretreatment time of between 10 seconds and 60 seconds to inhibit development of microorganisms present on said materials without significantly altering the physical properties of said materials;
- and then
- exposing said materials to a low temperature plasma of organic monomer gas for a treatment time ranging from 30 to 3600 seconds to form a thin layer of polymer material on the surface of said materials.
A method for neutralizing microorganisms on archival materials and preserving the materials against humidity and ultraviolet radiation, comprising the steps of:
- first exposing said materials to a lower temperature argon plasma at a pressure of between 0.01 to 10 Torr, a power input frequency of between 1 and 40 MgHz with a specific discharge power of between 0.003 and 3.0 Wt/cm.sup.3, for a treatment time ranging from 10 to 60 seconds;
- then exposing said materials to a low temperature plasma of methane gas generated by a power source of 1 to 40 MHz with a specific discharge power of 0.003 to 3.0 Wt/cm.sup.3 at a pressure of 0.01 to 10 Torr for a treatment time ranging from 30 to 3600 seconds to form a thin layer of polymer material on the surface of said material.