Method for making ceramic matrix composites
AssigneeCorning Incorporated
InventorsRoger A. Allaire, Victor F. Janas
Life of this patent
Estimating the term…
Abstract
A method for making a ceramic matrix composite article wherein a dispersion of a ceramic matrix powder in a wax-containing thermoplastic vehicle is applied to an inorganic fiber reinforcement material to form a prepreg material such as a prepreg tow, and the tow is collected and formed into a preform for the article which is then subjected to binder burnout and consolidation, wherein the prepreg material is heated to a temperature sufficient to evaporate at least about 50% by weight of the wax component therefrom prior to the collection and forming of the material into the preform.
Claims11
In the method for making a ceramic matrix composite article wherein a dispersion of a ceramic matrix powder in a thermoplastic vehicle is applied to an inorganic fiber reinforcement material to form a prepreg material, the thermoplastic vehicle comprising, in weight percent, about 10-40% of polymer binder components, 35-90% of volatile wax components, at least 60% total of polymer binder and volatile was components, and 0-35% of optional additives selected from the group consisting of surface-active dispersants, polymeric plasticizers, and non-volatile waxes, the prepreg material is collected, the collected prepreg material is formed into a preform for the article, the preform for the article is subjected to binder burnout, and the preform is thereafter consolidated by the application of heat and pressure to form the article, the improvement wherein:
- prior to forming the collected prepreg material into the preform, the prepreg is heated to a temperature sufficient to evaporate at least about 50% by weight of the volatile wax components from the thermoplastic vehicle but insufficient to remove the organic polymer binder component therefrom.
A method for making a ceramic matrix composite article which comprises the steps of:
- (i) applying to an inorganic fiber tow a dispersion of a ceramic matrix powder in a thermoplastic vehicle, the thermoplastic vehicle comprising, in weight percent, about 10-40% of polymer binder components, 35-90% of volatile wax components, at least 60% total of polymer binder and volatile wax components, and 0-35% of optional additives selected from the group consisting of surface-active dispersants, polymeric plasticizers, and non-volatile waxes, thus to provide a prepreg fiber tow;
- (ii) heating the prepreg fiber tow to a temperature and for a time sufficient to evaporate at least about 50% by weight of the volatile wax components from the thermoplastic vehicle but insufficient to remove the organic polymer binder component therefrom, thus to provide a dewaxed fiber tow;
- (iii) collecting the dewaxed fiber tow and forming it into a prepreg shape;
- (iv) forming the prepreg shape into a preform for the ceramic matrix composite article;
- (v) heat treating the preform to remove remaining vehicle constituents therefrom;
- and
- (vi) consolidating the preform by the application of heat and pressure to form the ceramic matrix composite article.